Preparation of TiAl15Si15 intermetallic alloy by mechanical alloying and the spark plasma sintering method

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F19%3A00505343" target="_blank" >RIV/68378271:_____/19:00505343 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/19:43919022 RIV/00025798:_____/19:00000124

Výsledek na webu

<a href="https://doi.org/10.1080/00325899.2019.1569812" target="_blank" >https://doi.org/10.1080/00325899.2019.1569812</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1080/00325899.2019.1569812" target="_blank" >10.1080/00325899.2019.1569812</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation of TiAl15Si15 intermetallic alloy by mechanical alloying and the spark plasma sintering method

Popis výsledku v původním jazyce

This work is devoted to the preparation of alloys based on intermetallic compounds in the Ti–Al–Si system by powder metallurgy using mechanical alloying and the spark plasma sintering (SPS) method. The aim was to describe the formation of intermetallic phases during mechanical alloying of TiAl15Si15 (wt-%) alloy and to consolidate the powder prepared by optimised conditions. Phase composition, microstructure and hardness of compacted alloy were determined. Four hours of mechanical alloying is sufficient time for preparation of pure elements free material composed only of intermetallic phases. After consolidation, the TiAl15Si15 alloy has a homogeneous structure composed of silicide (Ti5Si3) in aluminide (TiAl) matrix. The hardness of the material reaches 865 ± 42 HV 5.

Název v anglickém jazyce

Preparation of TiAl15Si15 intermetallic alloy by mechanical alloying and the spark plasma sintering method

Popis výsledku anglicky

This work is devoted to the preparation of alloys based on intermetallic compounds in the Ti–Al–Si system by powder metallurgy using mechanical alloying and the spark plasma sintering (SPS) method. The aim was to describe the formation of intermetallic phases during mechanical alloying of TiAl15Si15 (wt-%) alloy and to consolidate the powder prepared by optimised conditions. Phase composition, microstructure and hardness of compacted alloy were determined. Four hours of mechanical alloying is sufficient time for preparation of pure elements free material composed only of intermetallic phases. After consolidation, the TiAl15Si15 alloy has a homogeneous structure composed of silicide (Ti5Si3) in aluminide (TiAl) matrix. The hardness of the material reaches 865 ± 42 HV 5.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Powder Metallurgy

ISSN

0032-5899

e-ISSN

—

Svazek periodika

62

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

54-60

Kód UT WoS článku

000458410800006

EID výsledku v databázi Scopus

2-s2.0-85060689393