Magnetic coercivity control by heat treatment in Heusler Ni-Mn-Ga(-B) single crystals

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F19%3A00509151" target="_blank" >RIV/68378271:_____/19:00509151 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/19:10399607

Výsledek na webu

<a href="http://hdl.handle.net/11104/0299923" target="_blank" >http://hdl.handle.net/11104/0299923</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.actamat.2019.02.045" target="_blank" >10.1016/j.actamat.2019.02.045</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Magnetic coercivity control by heat treatment in Heusler Ni-Mn-Ga(-B) single crystals

Popis výsledku v původním jazyce

The combination of enlarged magnetic coercivity and magnetic shape memory (MSM) functionality is essential for novel magnetomechanical effects in MSM alloys. We found that increasing the density of thermal antiphase boundaries (APBs) provides a method to increase the magnetic coercivity without deteriorating the MSM functionality. APB density was controlled by different heat treatments in Ni–Mn–Ga (–B) MSM single crystals with five-layered modulated martensite structure. Slow cooling ∼1 K/min of Ni–Mn–Ga through the B2′–L21 transition resulted in a low density ( < 1/micrometer) of APBs observed by magnetic force microscopy and low coercivity <2 mT. Water quenching resulted in fine magnetic and APB patterns and enlarged the coercivity to 24 mT at room temperature, and this further increased with decreasing temperature up to 41 mT at 10 K.

Název v anglickém jazyce

Magnetic coercivity control by heat treatment in Heusler Ni-Mn-Ga(-B) single crystals

Popis výsledku anglicky

The combination of enlarged magnetic coercivity and magnetic shape memory (MSM) functionality is essential for novel magnetomechanical effects in MSM alloys. We found that increasing the density of thermal antiphase boundaries (APBs) provides a method to increase the magnetic coercivity without deteriorating the MSM functionality. APB density was controlled by different heat treatments in Ni–Mn–Ga (–B) MSM single crystals with five-layered modulated martensite structure. Slow cooling ∼1 K/min of Ni–Mn–Ga through the B2′–L21 transition resulted in a low density ( < 1/micrometer) of APBs observed by magnetic force microscopy and low coercivity <2 mT. Water quenching resulted in fine magnetic and APB patterns and enlarged the coercivity to 24 mT at room temperature, and this further increased with decreasing temperature up to 41 mT at 10 K.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Materialia

ISSN

1359-6454

e-ISSN

—

Svazek periodika

169

Číslo periodika v rámci svazku

May

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

13

Strana od-do

109-121

Kód UT WoS článku

000465365300011

EID výsledku v databázi Scopus

2-s2.0-85062865043