Effect of high temperature on the microstructural evolution of fiber reinforced geopolymer composite

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F19%3A00512072" target="_blank" >RIV/68378271:_____/19:00512072 - isvavai.cz</a>

Výsledek na webu

<a href="http://hdl.handle.net/11104/0302282" target="_blank" >http://hdl.handle.net/11104/0302282</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.heliyon.2019.e01779" target="_blank" >10.1016/j.heliyon.2019.e01779</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of high temperature on the microstructural evolution of fiber reinforced geopolymer composite

Popis výsledku v původním jazyce

Physical evolution of geopolymeric minerals derived from metakaolin and synthesized with sodium, mixed-alkali and potassium activating solutions (Na- K) during thermal exposure. The geopolymer composites were prepared with 40 V% of fiber reinforcement such as carbon, E-glass, and basalt at the direction of in plain. Fiber reinforced geopolymer composites were exposed to the room and elevated temperatures inside the oven at air medium for a period of 30 min. The durability of the composites and internal structures with surface microstructures were examined after high temperature exposures. According to the results, geopolymer implied a prominent influence on the thermal shrinkage with the increasing of Si/Al ratios. This was attributed to the densification caused by reduction in porosity during dehydroxylation and sintering. In the case of carbon fiber reinforced composite shows transition in strength after 600 °C due to the oxide protective layer that increases the flexural strength and toughness of the composite. The flexural strength of the carbon reinforced composite increases from 17.8 to 55.8 MPa at 1000 °C.

Název v anglickém jazyce

Effect of high temperature on the microstructural evolution of fiber reinforced geopolymer composite

Popis výsledku anglicky

Physical evolution of geopolymeric minerals derived from metakaolin and synthesized with sodium, mixed-alkali and potassium activating solutions (Na- K) during thermal exposure. The geopolymer composites were prepared with 40 V% of fiber reinforcement such as carbon, E-glass, and basalt at the direction of in plain. Fiber reinforced geopolymer composites were exposed to the room and elevated temperatures inside the oven at air medium for a period of 30 min. The durability of the composites and internal structures with surface microstructures were examined after high temperature exposures. According to the results, geopolymer implied a prominent influence on the thermal shrinkage with the increasing of Si/Al ratios. This was attributed to the densification caused by reduction in porosity during dehydroxylation and sintering. In the case of carbon fiber reinforced composite shows transition in strength after 600 °C due to the oxide protective layer that increases the flexural strength and toughness of the composite. The flexural strength of the carbon reinforced composite increases from 17.8 to 55.8 MPa at 1000 °C.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Heliyon

ISSN

2405-8440

e-ISSN

—

Svazek periodika

5

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

1-10

Kód UT WoS článku

000473561400204

EID výsledku v databázi Scopus

2-s2.0-85066148420