Temperature influence on Er:GGAG crystal spectroscopic properties and its lasing at 3 μm

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F20%3A00534820" target="_blank" >RIV/68378271:_____/20:00534820 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1117/12.2541965" target="_blank" >http://dx.doi.org/10.1117/12.2541965</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1117/12.2541965" target="_blank" >10.1117/12.2541965</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Temperature influence on Er:GGAG crystal spectroscopic properties and its lasing at 3 μm

Popis výsledku v původním jazyce

The spectroscopic and laser properties of Er:GGAG active medium, in temperature range from 80 K to 300 K, are presented in this work. The sample of Er:GGAG (20 at. % of Er3+) crystal had face-polished plan-parallel faces without anti-reflection coatings (thickness 3.6 mm). During all experiments the Er:GGAG was attached to temperature controlled copper holder and it was placed in a vacuum chamber. The transmission and emission spectra together with the fluorescence decay time were measured depending on temperature.

Název v anglickém jazyce

Temperature influence on Er:GGAG crystal spectroscopic properties and its lasing at 3 μm

Popis výsledku anglicky

The spectroscopic and laser properties of Er:GGAG active medium, in temperature range from 80 K to 300 K, are presented in this work. The sample of Er:GGAG (20 at. % of Er3+) crystal had face-polished plan-parallel faces without anti-reflection coatings (thickness 3.6 mm). During all experiments the Er:GGAG was attached to temperature controlled copper holder and it was placed in a vacuum chamber. The transmission and emission spectra together with the fluorescence decay time were measured depending on temperature.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

<a href="/cs/project/EF16_019%2F0000760" target="_blank" >EF16_019/0000760: Fyzika pevných látek pro 21. století</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Solid State Lasers XXIX: Technology and Devices

ISBN

978-1-5106-3282-0

ISSN

0277-786X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

SPIE

Místo vydání

Bellingham

Místo konání akce

San Francisco

Datum konání akce

4. 2. 2020

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000568169600040