Proven technology of Laser Shock Peening (LSP) process for the cavitation erosion resistance improvement

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F20%3A00538617" target="_blank" >RIV/68378271:_____/20:00538617 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Proven technology of Laser Shock Peening (LSP) process for the cavitation erosion resistance improvement

Popis výsledku v původním jazyce

Development of the Laser Shock Peening (LSP) process which when applied can improve the resistance to the cavitation erosion in pumps. The basic principle of the LSP technology The high-energy laser after passing the confining medium is forming a high-pressure plasma. By this principle, shock waves are generated and they are plastically deforming the material and inducing deep compressed residual stresses. In such a principle, certain mechanical properties of the material are changed and typical improvements are prolonged fatigue life, prevention of the corrosion stress cracking, or wear resistance improvement. Additionally, the hardness can be improved as well. Cavitation erosion is a fatigue driven phenomenon, and by applying the LSP the cavitation erosion can be reduced and slowed down. The LSP was applied to the blades which in the end form the pump impeller. The blades are made of stainless steel 304 (1.4306) and stainless steel 321 (1.4541).

Název v anglickém jazyce

Proven technology of Laser Shock Peening (LSP) process for the cavitation erosion resistance improvement

Popis výsledku anglicky

Development of the Laser Shock Peening (LSP) process which when applied can improve the resistance to the cavitation erosion in pumps. The basic principle of the LSP technology The high-energy laser after passing the confining medium is forming a high-pressure plasma. By this principle, shock waves are generated and they are plastically deforming the material and inducing deep compressed residual stresses. In such a principle, certain mechanical properties of the material are changed and typical improvements are prolonged fatigue life, prevention of the corrosion stress cracking, or wear resistance improvement. Additionally, the hardness can be improved as well. Cavitation erosion is a fatigue driven phenomenon, and by applying the LSP the cavitation erosion can be reduced and slowed down. The LSP was applied to the blades which in the end form the pump impeller. The blades are made of stainless steel 304 (1.4306) and stainless steel 321 (1.4541).

Druh

Z_tech - Ověřená technologie

CEP obor

—

OECD FORD obor

20301 - Mechanical engineering

Projekt

<a href="/cs/project/TN01000038" target="_blank" >TN01000038: Národní centrum kompetence pro materiály, pokročilé technologie, povlakování a jejich aplikace</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Interní identifikační kód produktu

OTSZ01/FZU/2020

Číselná identifikace

OTSZ01/FZU/2020

Technické parametry

Aplikace technologie Laser shock peening na materiál vystavený kavitační erozi může výrazně prodloužit životnost zpracované součásti. Bylo experimentáně změřeno, že vyvolaná povrchová tlaková zbytková

Ekonomické parametry

Výsledky projektu budou využity pro další projekty a aplikace zaměřené na zvýšení korozní odolnosti. Tyto aplikace by měly generovat komerční příjem v závislosti na počtu aplikací a průmyslových partnerů.

Kategorie aplik. výsledku dle nákladů

—

IČO vlastníka výsledku

68378271

Název vlastníka

Fyzikální ústav AV ČR, v. v. i.

Stát vlastníka

CZ - Česká republika

Druh možnosti využití

A - K využití výsledku jiným subjektem je vždy nutné nabytí licence

Požadavek na licenční poplatek

A - Poskytovatel licence na výsledek požaduje licenční poplatek

Adresa www stránky s výsledkem

—