A new lithium-rich zeolitic 10-MR zincolithosilicate MZS-1 hydrothermally synthesized under high pressure and characterized by 3D electron diffraction
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F21%3A00541703" target="_blank" >RIV/68378271:_____/21:00541703 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.1002/ejic.202000939" target="_blank" >https://doi.org/10.1002/ejic.202000939</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/ejic.202000939" target="_blank" >10.1002/ejic.202000939</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
A new lithium-rich zeolitic 10-MR zincolithosilicate MZS-1 hydrothermally synthesized under high pressure and characterized by 3D electron diffraction
Popis výsledku v původním jazyce
We report the structure of a new high lithium content zincolithosilicate (MZS-1) obtained after hydrothermal treatment under high pressure from a glass precursor. After synthesis microcrystalline mixture of phases was obtained among which the main phase was unknown. Due to the sub micrometric size of the crystallites its structure was determined from precession-assisted 3D electron diffraction measured at 100 K and refined using the dynamical theory of diffraction. More accurate lattice parameters are obtained from Rietveld refinement of synchrotron powder data collected at the ambient temperature.
Název v anglickém jazyce
A new lithium-rich zeolitic 10-MR zincolithosilicate MZS-1 hydrothermally synthesized under high pressure and characterized by 3D electron diffraction
Popis výsledku anglicky
We report the structure of a new high lithium content zincolithosilicate (MZS-1) obtained after hydrothermal treatment under high pressure from a glass precursor. After synthesis microcrystalline mixture of phases was obtained among which the main phase was unknown. Due to the sub micrometric size of the crystallites its structure was determined from precession-assisted 3D electron diffraction measured at 100 K and refined using the dynamical theory of diffraction. More accurate lattice parameters are obtained from Rietveld refinement of synchrotron powder data collected at the ambient temperature.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
European Journal of Inorganic Chemistry
ISSN
1434-1948
e-ISSN
1099-0682
Svazek periodika
2021
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
11
Strana od-do
628-638
Kód UT WoS článku
000614758200001
EID výsledku v databázi Scopus
2-s2.0-85100552585