Tribological behavior of NiTi alloy produced by spark plasma sintering method
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F21%3A00553043" target="_blank" >RIV/68378271:_____/21:00553043 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989592:15310/21:73610861 RIV/60461373:22810/21:43922149
Výsledek na webu
<a href="http://hdl.handle.net/11104/0328095" target="_blank" >http://hdl.handle.net/11104/0328095</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/coatings11101246" target="_blank" >10.3390/coatings11101246</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Tribological behavior of NiTi alloy produced by spark plasma sintering method
Popis výsledku v původním jazyce
The tribological behaviors of NiTi alloy produced by the spark plasma sintering (SPS) method before and after annealing were investigated at various loading conditions via indentation, scratch, and wear tests. Indentation tests were performed by a pyramidal Berkovich indenter, while scratch and wear tests were carried out by a diamond Rockwell spherical indenter at room temperature. The annealing of the as-prepared samples was performed at 350, 450, and 550C in the ambient atmosphere. The alloy annealed at 350 C showed a higher hardness compared to the other annealed alloys. The scratch and wear resistance of the annealed sample at 350C showed a better performance in comparison to the other samples under a constant load. The high wear resistance of the annealed NiTi alloy may be attributed to its metastable R-phase.
Název v anglickém jazyce
Tribological behavior of NiTi alloy produced by spark plasma sintering method
Popis výsledku anglicky
The tribological behaviors of NiTi alloy produced by the spark plasma sintering (SPS) method before and after annealing were investigated at various loading conditions via indentation, scratch, and wear tests. Indentation tests were performed by a pyramidal Berkovich indenter, while scratch and wear tests were carried out by a diamond Rockwell spherical indenter at room temperature. The annealing of the as-prepared samples was performed at 350, 450, and 550C in the ambient atmosphere. The alloy annealed at 350 C showed a higher hardness compared to the other annealed alloys. The scratch and wear resistance of the annealed sample at 350C showed a better performance in comparison to the other samples under a constant load. The high wear resistance of the annealed NiTi alloy may be attributed to its metastable R-phase.
Klasifikace
Druh
J<sub>SC</sub> - Článek v periodiku v databázi SCOPUS
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Coatings
ISSN
2079-6412
e-ISSN
2079-6412
Svazek periodika
11
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
18
Strana od-do
1246
Kód UT WoS článku
000815328000001
EID výsledku v databázi Scopus
2-s2.0-85118356810