Crystal growth of La2Zr2O7 by micro-pulling-down method using Mo and W crucibles

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F21%3A00561147" target="_blank" >RIV/68378271:_____/21:00561147 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1016/j.jcrysgro.2021.126357" target="_blank" >https://doi.org/10.1016/j.jcrysgro.2021.126357</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jcrysgro.2021.126357" target="_blank" >10.1016/j.jcrysgro.2021.126357</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Crystal growth of La2Zr2O7 by micro-pulling-down method using Mo and W crucibles

Popis výsledku v původním jazyce

La2Zr2O7 crystals with a melting point of 2283 °C are grown via the micro-pulling-down (μ-PD) method using Mo and W crucibles to expand the possibility of material research of functional single crystals with high melting points by the μ-PD method. La2Zr2O7 crystals grown using Mo and W crucibles under an Ar + 3% H2 atmosphere are composed of a La2Zr2O7 main phase, which includes Mo and W. However, a La2Zr2O7 crystal without W can be grown under an Ar atmosphere using the μ-PD method using a W crucible and deoxygenated ZrO2 insulators. After post-annealing in air at 1000 °C, the La2Zr2O7 crystal without W becomes colorless and transparent, indicating a transmittance exceeding 70% in wavelengths ranging from 450 to 800 nm.n

Název v anglickém jazyce

Crystal growth of La2Zr2O7 by micro-pulling-down method using Mo and W crucibles

Popis výsledku anglicky

La2Zr2O7 crystals with a melting point of 2283 °C are grown via the micro-pulling-down (μ-PD) method using Mo and W crucibles to expand the possibility of material research of functional single crystals with high melting points by the μ-PD method. La2Zr2O7 crystals grown using Mo and W crucibles under an Ar + 3% H2 atmosphere are composed of a La2Zr2O7 main phase, which includes Mo and W. However, a La2Zr2O7 crystal without W can be grown under an Ar atmosphere using the μ-PD method using a W crucible and deoxygenated ZrO2 insulators. After post-annealing in air at 1000 °C, the La2Zr2O7 crystal without W becomes colorless and transparent, indicating a transmittance exceeding 70% in wavelengths ranging from 450 to 800 nm.n

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Crystal Growth

ISSN

0022-0248

e-ISSN

1873-5002

Svazek periodika

575

Číslo periodika v rámci svazku

Dec

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

126357

Kód UT WoS článku

000707447800001

EID výsledku v databázi Scopus

2-s2.0-85116537173