Optical and scintillation characteristics of Lu2Y(Al5-xGax)O12:Ce,Mg multicomponent garnet crystals
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F22%3A00564930" target="_blank" >RIV/68378271:_____/22:00564930 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.1016/j.optmat.2022.113186" target="_blank" >https://doi.org/10.1016/j.optmat.2022.113186</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.optmat.2022.113186" target="_blank" >10.1016/j.optmat.2022.113186</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Optical and scintillation characteristics of Lu2Y(Al5-xGax)O12:Ce,Mg multicomponent garnet crystals
Popis výsledku v původním jazyce
Optical and scintillation characteristics of Mg2+-codoped Lu2Y(Al5-xGax)O12:Ce (x = 2, 3) multicomponent garnet crystals grown by the micro-pulling down method were investigated. At RT, the shortening of scintillation decay time and a decrease of light yield (LY) value measured for a higher Ga containing samples can be explained by thermal ionization of the Ce3+ 5d1 excited state. At 662 keV γ-rays, Lu2YAl3Ga2O12: Ce, 0.05%Mg exhibits high LY value of 29,000 ph/MeV along with scintillation decay times of 50 ns (86%) + 73 ns (14%). Co-doping with larger Mg2+ content leads to a decrease of LY value, scintillation decay time, and afterglow level. Radioluminescence quenching observed at low temperature region in correlation with large thermoluminescence peaks can be caused by trapping of electrons at intrinsic shallow traps.
Název v anglickém jazyce
Optical and scintillation characteristics of Lu2Y(Al5-xGax)O12:Ce,Mg multicomponent garnet crystals
Popis výsledku anglicky
Optical and scintillation characteristics of Mg2+-codoped Lu2Y(Al5-xGax)O12:Ce (x = 2, 3) multicomponent garnet crystals grown by the micro-pulling down method were investigated. At RT, the shortening of scintillation decay time and a decrease of light yield (LY) value measured for a higher Ga containing samples can be explained by thermal ionization of the Ce3+ 5d1 excited state. At 662 keV γ-rays, Lu2YAl3Ga2O12: Ce, 0.05%Mg exhibits high LY value of 29,000 ph/MeV along with scintillation decay times of 50 ns (86%) + 73 ns (14%). Co-doping with larger Mg2+ content leads to a decrease of LY value, scintillation decay time, and afterglow level. Radioluminescence quenching observed at low temperature region in correlation with large thermoluminescence peaks can be caused by trapping of electrons at intrinsic shallow traps.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Optical Materials
ISSN
0925-3467
e-ISSN
1873-1252
Svazek periodika
134
Číslo periodika v rámci svazku
Dec.
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
8
Strana od-do
113186
Kód UT WoS článku
000890421500005
EID výsledku v databázi Scopus
2-s2.0-85141447132