The influence of tilt on Berkovich indentation of a steel sample using FEM analysis and nanoindentation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F22%3A00579663" target="_blank" >RIV/68378271:_____/22:00579663 - isvavai.cz</a>
Výsledek na webu
<a href="https://sciendo.com/article/10.2478/pmp-2022-0007" target="_blank" >https://sciendo.com/article/10.2478/pmp-2022-0007</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.2478/pmp-2022-0007" target="_blank" >10.2478/pmp-2022-0007</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The influence of tilt on Berkovich indentation of a steel sample using FEM analysis and nanoindentation
Popis výsledku v původním jazyce
The main shape deviations of a Berkovich indenter are the indenter bluntness and indenter tilt. The influence of the Berkovich indenter tilt on the results of the FEM modelling of steel nanoindentation is evaluated in this paper. The indenter tilt has an impact on the indentation curves and contact area. The X5CrNiCuNb 16-4 steel nanoindentation was modelled by FEM and the indentation curves were obtained. The Berkovich indenter was blunted and the tilt of the indenter was changed to determine its influence on the indentation curves. The results showed that growing tilt shifts the indentation curves to higher values of indentation forces and makes unloading curves steeper which is in agreement with a larger contact area. The calculated indentation curves were compared with the experimental indentation curves and the impact of the indenter tilt to the indentation curves was determined.
Název v anglickém jazyce
The influence of tilt on Berkovich indentation of a steel sample using FEM analysis and nanoindentation
Popis výsledku anglicky
The main shape deviations of a Berkovich indenter are the indenter bluntness and indenter tilt. The influence of the Berkovich indenter tilt on the results of the FEM modelling of steel nanoindentation is evaluated in this paper. The indenter tilt has an impact on the indentation curves and contact area. The X5CrNiCuNb 16-4 steel nanoindentation was modelled by FEM and the indentation curves were obtained. The Berkovich indenter was blunted and the tilt of the indenter was changed to determine its influence on the indentation curves. The results showed that growing tilt shifts the indentation curves to higher values of indentation forces and makes unloading curves steeper which is in agreement with a larger contact area. The calculated indentation curves were compared with the experimental indentation curves and the impact of the indenter tilt to the indentation curves was determined.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/TN01000038" target="_blank" >TN01000038: Národní centrum kompetence pro materiály, pokročilé technologie, povlakování a jejich aplikace</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the conference Local Mechanical Properties
ISBN
—
ISSN
1339-4533
e-ISSN
1339-4533
Počet stran výsledku
9
Strana od-do
53-61
Název nakladatele
de Gruyter
Místo vydání
Warszawa
Místo konání akce
Košice
Datum konání akce
11. 5. 2022
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—