Fracture toughness of cement paste assessed with micro-scratch and acoustic emission

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F22%3A00579670" target="_blank" >RIV/68378271:_____/22:00579670 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21110/23:00367186

Výsledek na webu

<a href="https://sciendo.com/article/10.2478/pmp-2022-0002" target="_blank" >https://sciendo.com/article/10.2478/pmp-2022-0002</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.2478/pmp-2022-0002" target="_blank" >10.2478/pmp-2022-0002</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture toughness of cement paste assessed with micro-scratch and acoustic emission

Popis výsledku v původním jazyce

Micro-scratch test was used to evaluate the fracture toughness of the main hydration products of ordinary Portland cement paste at the microscale. The evaluation was done with the aid of scanning electron microscopy and acoustic emission (AE) signals. Portlandite was found to be the only phase where AE detected elastic waves due to cracking during microindentation and micro-scratch test. Such behavior simplifies phase separation during the evaluation process of the micro-scratch test. The micro-scale fracture toughness results obtained from the tests were found in close agreement with other available experiments and models in the literature.n

Název v anglickém jazyce

Fracture toughness of cement paste assessed with micro-scratch and acoustic emission

Popis výsledku anglicky

Micro-scratch test was used to evaluate the fracture toughness of the main hydration products of ordinary Portland cement paste at the microscale. The evaluation was done with the aid of scanning electron microscopy and acoustic emission (AE) signals. Portlandite was found to be the only phase where AE detected elastic waves due to cracking during microindentation and micro-scratch test. Such behavior simplifies phase separation during the evaluation process of the micro-scratch test. The micro-scale fracture toughness results obtained from the tests were found in close agreement with other available experiments and models in the literature.n

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA21-11965S" target="_blank" >GA21-11965S: Výzkum mikrostruktury a simulace sdružených fyzikálních polí v betonu při elektromigračním léčení</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the conference Local Mechanical Properties

ISBN

—

ISSN

1339-4533

e-ISSN

1339-4533

Počet stran výsledku

7

Strana od-do

7-13

Název nakladatele

de Gruyter

Místo vydání

Warszawa

Místo konání akce

Košice

Datum konání akce

11. 5. 2022

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—