Modulated martensite in NiTi shape memory alloy exposed to high stress at high temperatures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F23%3A00574352" target="_blank" >RIV/68378271:_____/23:00574352 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1016/j.actamat.2023.119250" target="_blank" >https://doi.org/10.1016/j.actamat.2023.119250</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.actamat.2023.119250" target="_blank" >10.1016/j.actamat.2023.119250</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Modulated martensite in NiTi shape memory alloy exposed to high stress at high temperatures

Popis výsledku v původním jazyce

NiTi shape memory wire was deformed in martensite state at low temperature −125 °C up to 750 MPa stress and subsequently heated far above the Af temperature while the stress 750 MPa was held constant. Under such conditions, the heated B19’ martensite in the wire was driven towards its thermomechanical stability limits and eventually transformed into plastically deformed austenite. In order to evaluate the mechanism by which such highly constrained reverse martensitic transformation proceeds, martensite variant microstructures and lattice defects evolving in the heated wire were analyzed by TEM and HRTEM.

Název v anglickém jazyce

Modulated martensite in NiTi shape memory alloy exposed to high stress at high temperatures

Popis výsledku anglicky

NiTi shape memory wire was deformed in martensite state at low temperature −125 °C up to 750 MPa stress and subsequently heated far above the Af temperature while the stress 750 MPa was held constant. Under such conditions, the heated B19’ martensite in the wire was driven towards its thermomechanical stability limits and eventually transformed into plastically deformed austenite. In order to evaluate the mechanism by which such highly constrained reverse martensitic transformation proceeds, martensite variant microstructures and lattice defects evolving in the heated wire were analyzed by TEM and HRTEM.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Materialia

ISSN

1359-6454

e-ISSN

1873-2453

Svazek periodika

258

Číslo periodika v rámci svazku

Oct

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

19

Strana od-do

119250

Kód UT WoS článku

001088416900001

EID výsledku v databázi Scopus

2-s2.0-85168307168