Effects of Sc3+ admixture on luminescence and scintillation properties of Ce3+-doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F23%3A00576151" target="_blank" >RIV/68378271:_____/23:00576151 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/23:10473335

Výsledek na webu

<a href="https://doi.org/10.1016/j.optmat.2023.114417" target="_blank" >https://doi.org/10.1016/j.optmat.2023.114417</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.optmat.2023.114417" target="_blank" >10.1016/j.optmat.2023.114417</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effects of Sc3+ admixture on luminescence and scintillation properties of Ce3+-doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films

Popis výsledku v původním jazyce

Effects of Sc3+ admixture on luminescence and scintillation properties were studied in Ce3+ - doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films grown by the isothermal liquid phase epitaxy technique. The Ce3+ photoluminescence (PL) was slightly blue shifted with increasing Sc content due to a decrease in crystal field splitting of the Ce3+ 5d levels. In addition, the thermal activation energy of PL quenching, estimated from the temperature dependence of PL decay times, decreased with increasing Sc content. Lu2YAl4ScO12:Ce exhibited the highest light yield (LY) value of 420 photons/MeV at 5.5 MeV α particles along with a fast scintillation decay time constant (τe) of 17.4 ns. At room temperature, the decrease of LY value with increasing Sc content could be attributed to the thermal ionization process.

Název v anglickém jazyce

Effects of Sc3+ admixture on luminescence and scintillation properties of Ce3+-doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films

Popis výsledku anglicky

Effects of Sc3+ admixture on luminescence and scintillation properties were studied in Ce3+ - doped Lu2Y(Al5-xScx)O12 (x = 1, 1.5, 2) garnet single-crystalline films grown by the isothermal liquid phase epitaxy technique. The Ce3+ photoluminescence (PL) was slightly blue shifted with increasing Sc content due to a decrease in crystal field splitting of the Ce3+ 5d levels. In addition, the thermal activation energy of PL quenching, estimated from the temperature dependence of PL decay times, decreased with increasing Sc content. Lu2YAl4ScO12:Ce exhibited the highest light yield (LY) value of 420 photons/MeV at 5.5 MeV α particles along with a fast scintillation decay time constant (τe) of 17.4 ns. At room temperature, the decrease of LY value with increasing Sc content could be attributed to the thermal ionization process.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Optical Materials

ISSN

0925-3467

e-ISSN

1873-1252

Svazek periodika

145

Číslo periodika v rámci svazku

Nov

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

114417

Kód UT WoS článku

001165070600001

EID výsledku v databázi Scopus

2-s2.0-85172922737