Effect of carburizing on fatigue life of highstrength steel specimen under push-pull loading
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F14%3A00430342" target="_blank" >RIV/68378297:_____/14:00430342 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.europment.org/library/2014/santorini/bypaper/MECHANICS/MECHANICS-00.pdf" target="_blank" >http://www.europment.org/library/2014/santorini/bypaper/MECHANICS/MECHANICS-00.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of carburizing on fatigue life of highstrength steel specimen under push-pull loading
Popis výsledku v původním jazyce
Many articles are dedicated to effect of surface layer on fatigue life. However, most of these articles are dedicated to the steels with nitride layer and only small number of papers is dedicated to the carburizing. Results of extended experimental investigation of fatigue resistance of plasma-carburized specimens made of the lowalloy high-strength steel are presented. The specimens were subjected to push-pull loading of different R-ratios. The application of plasma carburizing can lead to about 25% increase in the fatigue resistance in the high cycle region (over 105 cycles). On the contrary, in the case of low cycle fatigue often has a negative effect on the service life.
Název v anglickém jazyce
Effect of carburizing on fatigue life of highstrength steel specimen under push-pull loading
Popis výsledku anglicky
Many articles are dedicated to effect of surface layer on fatigue life. However, most of these articles are dedicated to the steels with nitride layer and only small number of papers is dedicated to the carburizing. Results of extended experimental investigation of fatigue resistance of plasma-carburized specimens made of the lowalloy high-strength steel are presented. The specimens were subjected to push-pull loading of different R-ratios. The application of plasma carburizing can lead to about 25% increase in the fatigue resistance in the high cycle region (over 105 cycles). On the contrary, in the case of low cycle fatigue often has a negative effect on the service life.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JM - Inženýrské stavitelství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advances in engineering mechanics and materials
ISBN
978-1-61804-241-5
ISSN
—
e-ISSN
—
Počet stran výsledku
4
Strana od-do
143-146
Název nakladatele
WSEAS Press
Místo vydání
Santorini
Místo konání akce
Santorini
Datum konání akce
17. 7. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—