Non-standard experimental tests of sandstone and its pre-cracking for fracture testing
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378297%3A_____%2F18%3A00489927" target="_blank" >RIV/68378297:_____/18:00489927 - isvavai.cz</a>
Výsledek na webu
<a href="http://iopscience.iop.org/article/10.1088/1757-899X/379/1/012029" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/379/1/012029</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1757-899X/379/1/012029" target="_blank" >10.1088/1757-899X/379/1/012029</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Non-standard experimental tests of sandstone and its pre-cracking for fracture testing
Popis výsledku v původním jazyce
The paper presents a methodology for investigating fracture phenomena in sandstone. It shows the preparation of test specimens with a cyclic loading generated crack, control of the test specimen preparation and verification by means of x-ray microCT and digital image correlation (DIC) techniques. There are also presented tests studying tensile and fatigue characteristics of arkose sandstone used i. a. for the construction of the medieval Charles Bridge in Prague where weather induced tensile damage and failure occurred. Finally, the new methodology for pre-cracking of the specimens was verified experimentally and fracture toughness was computed.
Název v anglickém jazyce
Non-standard experimental tests of sandstone and its pre-cracking for fracture testing
Popis výsledku anglicky
The paper presents a methodology for investigating fracture phenomena in sandstone. It shows the preparation of test specimens with a cyclic loading generated crack, control of the test specimen preparation and verification by means of x-ray microCT and digital image correlation (DIC) techniques. There are also presented tests studying tensile and fatigue characteristics of arkose sandstone used i. a. for the construction of the medieval Charles Bridge in Prague where weather induced tensile damage and failure occurred. Finally, the new methodology for pre-cracking of the specimens was verified experimentally and fracture toughness was computed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
IOP Conference Series: Materials Science and Engineering
ISBN
—
ISSN
1757-8981
e-ISSN
1757-899X
Počet stran výsledku
7
Strana od-do
—
Název nakladatele
IOP Publishing
Místo vydání
Bristol
Místo konání akce
Blansko
Datum konání akce
29. 5. 2018
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—