Thermal and Hygric Properties of a Carbon-Fiber Reinforced Cement Composite Material after Thermal Load

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F02%3A01075453" target="_blank" >RIV/68407700:21110/02:01075453 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Thermal and Hygric Properties of a Carbon-Fiber Reinforced Cement Composite Material after Thermal Load

Popis výsledku v původním jazyce

Moisture diffusivity, high temperature thermal diffusivity, room temperature thermal conductivity, specific heat and water vapor permeability of a carbon fiber reinforced cement composite material are measured on specimens thermally loaded by subjectingto a temperature up to 1000 0C prior to the measurement. The linear thermal expansion coefficient is due to the character of the measuring method measured in the high temperature range to 1000 0C without any pre-treatment. The values of moisture diffusivity are found to depend on the thermal load in a very significant way, the maximum increase compared to the unloaded samples being two orders of magnitude. The changes of other studied parameters are lower but also significant. The water vapor permeability increases up to 4.5 times, the room temperature thermal conductivity decreases by 25% and the specific heat decreases by 20%

Název v anglickém jazyce

Thermal and Hygric Properties of a Carbon-Fiber Reinforced Cement Composite Material after Thermal Load

Popis výsledku anglicky

Moisture diffusivity, high temperature thermal diffusivity, room temperature thermal conductivity, specific heat and water vapor permeability of a carbon fiber reinforced cement composite material are measured on specimens thermally loaded by subjectingto a temperature up to 1000 0C prior to the measurement. The linear thermal expansion coefficient is due to the character of the measuring method measured in the high temperature range to 1000 0C without any pre-treatment. The values of moisture diffusivity are found to depend on the thermal load in a very significant way, the maximum increase compared to the unloaded samples being two orders of magnitude. The changes of other studied parameters are lower but also significant. The water vapor permeability increases up to 4.5 times, the room temperature thermal conductivity decreases by 25% and the specific heat decreases by 20%

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Tagungsbeiträge Proceedings

ISBN

3-86005-322-1

ISSN

—

e-ISSN

—

Počet stran výsledku

9

Strana od-do

351-359

Název nakladatele

Technische Universität Dresden

Místo vydání

Dresden

Místo konání akce

Dresden

Datum konání akce

26. 9. 2002

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—