Vysokoteplotní vlastnosti kompozitních stavebních materiálů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F04%3A01099890" target="_blank" >RIV/68407700:21110/04:01099890 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

High-Temperature Properties of Composite Building Materials

Popis výsledku v původním jazyce

Fiber reinforced cement composites exhibited significantly better thermal properties in the high temperature range compared to the cement composites without any reinforcement. The positive effect of both glass fibers and carbon fibers consisted clearly in their good adhesion to the cement matrix so that the matrix was kept together even after serious damage due to the cement decomposition processes, and wide cracks did not appear as in the case of cement composites without any reinforcement. Therefore,it can be concluded that the studied fiber reinforced composites have a reasonably good thermal resistance and can be conveniently used for the high temperature protection of building structures.

Název v anglickém jazyce

High-Temperature Properties of Composite Building Materials

Popis výsledku anglicky

Fiber reinforced cement composites exhibited significantly better thermal properties in the high temperature range compared to the cement composites without any reinforcement. The positive effect of both glass fibers and carbon fibers consisted clearly in their good adhesion to the cement matrix so that the matrix was kept together even after serious damage due to the cement decomposition processes, and wide cracks did not appear as in the case of cement composites without any reinforcement. Therefore,it can be concluded that the studied fiber reinforced composites have a reasonably good thermal resistance and can be conveniently used for the high temperature protection of building structures.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA103%2F04%2F0139" target="_blank" >GA103/04/0139: Analýza vlastností alkalicky aktivovaných alumosilikátových materiálů namáhaných vysokými teplotami</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Roczniki Inźynierii Budowlanej

ISSN

1505-8425

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

31-36

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—