Cement Grains with Surface-Synthesized Carbon Nanofibers: Mechanical Properties and Nanostructure

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F11%3A00182751" target="_blank" >RIV/68407700:21110/11:00182751 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.nanocon.cz/" target="_blank" >http://www.nanocon.cz/</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Cement Grains with Surface-Synthesized Carbon Nanofibers: Mechanical Properties and Nanostructure

Popis výsledku v původním jazyce

Carbon nanofibers were synthesized directly on the surfaces of Portland cement grains. Mixing this new carbon/cement material with ordinary cement creates a modified cementitous substance, where carbon is perfectly dispersed in the volume. Previous attempts to create nano-reinforced composite materials suffered from flocculation and improper dispersion of separately added nanofibers/nanotubes. Now, the hybrid material can be intermixed directly with water and/or sand, creating strong and brittle composite similar to ordinary cement paste/mortar. The composites with weight fractions of carbon nanofibers/paste in the ranges 0-0.038 were prepared and mechanically tested. Slight increase in fracture energy and compressive strength was measured even in thelow carbon weigh fraction 0.019.

Název v anglickém jazyce

Cement Grains with Surface-Synthesized Carbon Nanofibers: Mechanical Properties and Nanostructure

Popis výsledku anglicky

Carbon nanofibers were synthesized directly on the surfaces of Portland cement grains. Mixing this new carbon/cement material with ordinary cement creates a modified cementitous substance, where carbon is perfectly dispersed in the volume. Previous attempts to create nano-reinforced composite materials suffered from flocculation and improper dispersion of separately added nanofibers/nanotubes. Now, the hybrid material can be intermixed directly with water and/or sand, creating strong and brittle composite similar to ordinary cement paste/mortar. The composites with weight fractions of carbon nanofibers/paste in the ranges 0-0.038 were prepared and mechanically tested. Slight increase in fracture energy and compressive strength was measured even in thelow carbon weigh fraction 0.019.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GD103%2F09%2FH078" target="_blank" >GD103/09/H078: Počítačová a experimentální analýza stavebních materiálů a jejich vícevrstvých systémů</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Nanocon 2011, Conference Proceedings

ISBN

978-80-87294-23-9

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

"nečíslov. (ArtNo=1308)"

Název nakladatele

TANGER, spol.s r.o

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 9. 2011

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—