Mechanical Properties of Kaolin during Heating
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F12%3A00205514" target="_blank" >RIV/68407700:21110/12:00205514 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.527.14" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.527.14</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.527.14" target="_blank" >10.4028/www.scientific.net/KEM.527.14</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical Properties of Kaolin during Heating
Popis výsledku v původním jazyce
Mechanical strength (MOR) and Young's modulus (YM) of Sedlec kaolin were measured using the three point-bending method and modulated force thermomechanical analysis (mf-TMA). An escape of the physically bound water (20-250 °C) strengthens the sample andYM and MOR increase their values significantly. MOR and YM lower their values as dehydroxylation starts at 400 °C. Both quantities, MOR and YM, pass through minimum in the dehydroxylation region (400-650 °C). Their next increase is probably caused by thevan der Waals forces acting between metakaolinite crystals and by the starting of the solid-state sintering. YM steeply increases above 950 °C as consequence of the solid-state sintering.
Název v anglickém jazyce
Mechanical Properties of Kaolin during Heating
Popis výsledku anglicky
Mechanical strength (MOR) and Young's modulus (YM) of Sedlec kaolin were measured using the three point-bending method and modulated force thermomechanical analysis (mf-TMA). An escape of the physically bound water (20-250 °C) strengthens the sample andYM and MOR increase their values significantly. MOR and YM lower their values as dehydroxylation starts at 400 °C. Both quantities, MOR and YM, pass through minimum in the dehydroxylation region (400-650 °C). Their next increase is probably caused by thevan der Waals forces acting between metakaolinite crystals and by the starting of the solid-state sintering. YM steeply increases above 950 °C as consequence of the solid-state sintering.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Key Engineering Materials
ISBN
—
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
6
Strana od-do
14-19
Název nakladatele
Trans Tech Publications
Místo vydání
Uetikon-Zurich
Místo konání akce
Tallin
Datum konání akce
18. 10. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000315125000003