Únavové vlastnosti betonových vzorků vystavených agresivnímu prostředí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F13%3A00207665" target="_blank" >RIV/68407700:21110/13:00207665 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

čeština

Název v původním jazyce

Únavové vlastnosti betonových vzorků vystavených agresivnímu prostředí

Popis výsledku v původním jazyce

High stress ranges caused by cyclic loading can result into accelerated crack propagation, higher deflection, structural stiffness reduction and consequently into fatigue failure. Agents contained in the aggressive environment (soluble salts, acids etc.)penetrate into the structure of concrete and reduce its matrix stiffness. The combination of these effects occurs e.g at bridges in urban environment or at crane tracks in chemical plants and leads to higher long-term structural damage. This paper presents current outcomes of long-term experimental programme which main goal is to quantify the combined effect of cyclic loading and aggressive environment on concrete specimens. The specimens are stored in saline lotion and subsequently in hydrochloric acid solution (HCl) for more than five years.

Název v anglickém jazyce

Fatigue Properties of Concrete Specimens Exposed to Aggressive Environment

Popis výsledku anglicky

High stress ranges caused by cyclic loading can result into accelerated crack propagation, higher deflection, structural stiffness reduction and consequently into fatigue failure. Agents contained in the aggressive environment (soluble salts, acids etc.)penetrate into the structure of concrete and reduce its matrix stiffness. The combination of these effects occurs e.g at bridges in urban environment or at crane tracks in chemical plants and leads to higher long-term structural damage. This paper presents current outcomes of long-term experimental programme which main goal is to quantify the combined effect of cyclic loading and aggressive environment on concrete specimens. The specimens are stored in saline lotion and subsequently in hydrochloric acid solution (HCl) for more than five years.

Druh

O - Ostatní výsledky

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-30441S" target="_blank" >GA13-30441S: Studium chování betonu vystaveného extrémnímu zatížení</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů