Mechanical and Rheological Properties of Aluminous Cement under High Temperatures
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F14%3A00218951" target="_blank" >RIV/68407700:21110/14:00218951 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.982.141" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.982.141</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.982.141" target="_blank" >10.4028/www.scientific.net/AMR.982.141</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical and Rheological Properties of Aluminous Cement under High Temperatures
Popis výsledku v původním jazyce
The following article deals with the relations between rheological behavior and strength characteristics of high aluminous cement paste. There were investigated the values of flow of fresh mixture (tested with Högermann´s table), tensile strength in bending and compressive strength at the age of 28 days on specimens 40 x 40 x 160 mm. The influence of high temperature was examined by exposure to 600 °C and 1000 °C. The results of provided experimental program confirm the fact that with increasing water-cement ration decreases compressive and tensile strength before and after temperature loading. Also was shown the effect of high temperature on refractory aluminous cement paste properties.
Název v anglickém jazyce
Mechanical and Rheological Properties of Aluminous Cement under High Temperatures
Popis výsledku anglicky
The following article deals with the relations between rheological behavior and strength characteristics of high aluminous cement paste. There were investigated the values of flow of fresh mixture (tested with Högermann´s table), tensile strength in bending and compressive strength at the age of 28 days on specimens 40 x 40 x 160 mm. The influence of high temperature was examined by exposure to 600 °C and 1000 °C. The results of provided experimental program confirm the fact that with increasing water-cement ration decreases compressive and tensile strength before and after temperature loading. Also was shown the effect of high temperature on refractory aluminous cement paste properties.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP104%2F12%2F0791" target="_blank" >GAP104/12/0791: Vláknové kompozity na bázi cementu pro vysokoteplotní aplikace</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Mechanical, Thermal and Hygric Properties of Buildings Materials
ISBN
978-3-03835-172-6
ISSN
1022-6680
e-ISSN
—
Počet stran výsledku
4
Strana od-do
141-144
Název nakladatele
TRANS TECH PUBLICATIONS LTD
Místo vydání
ZURICH
Místo konání akce
Zahrádky
Datum konání akce
23. 7. 2014
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—