Performance of Plasma Treated Polymer Macro-Fibers

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F16%3A00243178" target="_blank" >RIV/68407700:21110/16:00243178 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Performance of Plasma Treated Polymer Macro-Fibers

Popis výsledku v původním jazyce

Concrix – commercial bi-components polyolefin macro-fibers (ø 0.5 mm, length 50 mm) made by BURG Group in Switzerland were plasma treated to attain the better adhesion with cement matrix. Fibers were exposed to oxygen treatment in inductively coupled plasma system by different times (from 5 to 480 seconds.). The influence of realized fiber surface treatments was observed by physical and mechanical methods: i) horizontal direct optical method enabling a measurement of fibers wettability, ii) fibers tensile strength tests, and iii) single-fiber pull-out tests from cement matrix. It turned out that fibers treated by plasma during 30 seconds reached the best ratio between their wettability and mechanical performance. While their contact angles decreased by ca. 50 %, tensile strength remained constant and cohesion with cement matrix increased by ca. 20 % in comparison with reference fibers.

Název v anglickém jazyce

Performance of Plasma Treated Polymer Macro-Fibers

Popis výsledku anglicky

Concrix – commercial bi-components polyolefin macro-fibers (ø 0.5 mm, length 50 mm) made by BURG Group in Switzerland were plasma treated to attain the better adhesion with cement matrix. Fibers were exposed to oxygen treatment in inductively coupled plasma system by different times (from 5 to 480 seconds.). The influence of realized fiber surface treatments was observed by physical and mechanical methods: i) horizontal direct optical method enabling a measurement of fibers wettability, ii) fibers tensile strength tests, and iii) single-fiber pull-out tests from cement matrix. It turned out that fibers treated by plasma during 30 seconds reached the best ratio between their wettability and mechanical performance. While their contact angles decreased by ca. 50 %, tensile strength remained constant and cohesion with cement matrix increased by ca. 20 % in comparison with reference fibers.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GA15-12420S" target="_blank" >GA15-12420S: Modifikace povrchů polymerní a skleněné mikro-výztuže pro aplikace ve stavebnictví</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Experimental Stresss Analysis 2016

ISBN

978-80-261-0624-1

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

Západočeská universita, Fakulta aplikovaných věd

Místo vydání

Plzeň

Místo konání akce

Srní

Datum konání akce

30. 5. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—