Cement Paste with Recycled Concrete Powder: Long Term Development of the Strength

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F16%3A00302164" target="_blank" >RIV/68407700:21110/16:00302164 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Cement Paste with Recycled Concrete Powder: Long Term Development of the Strength

Popis výsledku v původním jazyce

Presented paper deals with using of a recycled concrete powder (RCP) modified by a high speed as microfiller and partial binder replacement in cement pastes. This approach allows to exposed unhydrated cement grains to further hydration. Such use of recycled concrete powder could lead to cost reduction of a concrete mixture. The flexural and compressive strength on samples made of Portland cement containing 0, 33, and 67 wt. % of a recycled concrete powder were determined. Those mechanical properties were determined in several times during 14 months. Results show that 33 wt. % cement replacement seems like limited value, when mechanical properties in long term scale are comparable with a reference sample. Samples with 67 wt. % of RCP had significantly lower strength compared with reference samples.

Název v anglickém jazyce

Cement Paste with Recycled Concrete Powder: Long Term Development of the Strength

Popis výsledku anglicky

Presented paper deals with using of a recycled concrete powder (RCP) modified by a high speed as microfiller and partial binder replacement in cement pastes. This approach allows to exposed unhydrated cement grains to further hydration. Such use of recycled concrete powder could lead to cost reduction of a concrete mixture. The flexural and compressive strength on samples made of Portland cement containing 0, 33, and 67 wt. % of a recycled concrete powder were determined. Those mechanical properties were determined in several times during 14 months. Results show that 33 wt. % cement replacement seems like limited value, when mechanical properties in long term scale are comparable with a reference sample. Samples with 67 wt. % of RCP had significantly lower strength compared with reference samples.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/TA04031256" target="_blank" >TA04031256: Rozvoj mechanicky aktivovaných materiálů na bázi recyklovaného betonu pro progresivní stabilizované a za studena recyklované konstrukční vrstvy</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Experimental Stresss Analysis 2016

ISBN

978-80-261-0624-1

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

Západočeská universita, Fakulta aplikovaných věd

Místo vydání

Plzeň

Místo konání akce

Srní

Datum konání akce

30. 5. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—