Influence of Compression Pressure on Young’s Modulus of Ceramic Samples
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F17%3A00319325" target="_blank" >RIV/68407700:21110/17:00319325 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1063/1.4994481" target="_blank" >http://dx.doi.org/10.1063/1.4994481</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1063/1.4994481" target="_blank" >10.1063/1.4994481</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of Compression Pressure on Young’s Modulus of Ceramic Samples
Popis výsledku v původním jazyce
The samples used in this study are created from a porcelain mixture. This mixture is a high strength aluminous porcelain which is used in electrotechnical engineering (high voltage insulators). The porcelain mixture contains clay, kaolin, feldspar, alumina, and small amount of other admixtures. The samples are made with three different compression pressures (80, 90, and 110 MPa). Impulse excitation technique, termodilatometry, and termogravimetry are used to determine Young’s modulus. The analyses are performed in the temperature range from 30 °C to 1100 °C with a heating rate of 5 °C/min in a static air atmosphere. It is found out that values of Young’s modulus do not increase linearly with the compression pressure.
Název v anglickém jazyce
Influence of Compression Pressure on Young’s Modulus of Ceramic Samples
Popis výsledku anglicky
The samples used in this study are created from a porcelain mixture. This mixture is a high strength aluminous porcelain which is used in electrotechnical engineering (high voltage insulators). The porcelain mixture contains clay, kaolin, feldspar, alumina, and small amount of other admixtures. The samples are made with three different compression pressures (80, 90, and 110 MPa). Impulse excitation technique, termodilatometry, and termogravimetry are used to determine Young’s modulus. The analyses are performed in the temperature range from 30 °C to 1100 °C with a heating rate of 5 °C/min in a static air atmosphere. It is found out that values of Young’s modulus do not increase linearly with the compression pressure.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20504 - Ceramics
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
THERMOPHYSICS 2017: 22nd International Meeting of Thermophysics 2017 and 4th Meeting of EnRe 2017
ISBN
978-0-7354-1546-1
ISSN
—
e-ISSN
1551-7616
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
American Institute of Physic AIP
Místo vydání
Santa Fe
Místo konání akce
Těrchová
Datum konání akce
12. 9. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000426600400006