Evaluation of Micromechanical Properties of Carbon Fiber Fabric Using Nanoindetation

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F17%3A00321992" target="_blank" >RIV/68407700:21110/17:00321992 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21720/17:00321992

Výsledek na webu

<a href="https://ojs.cvut.cz/ojs/index.php/APP/article/view/4630" target="_blank" >https://ojs.cvut.cz/ojs/index.php/APP/article/view/4630</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.14311/APP.2017.13.0066" target="_blank" >10.14311/APP.2017.13.0066</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Evaluation of Micromechanical Properties of Carbon Fiber Fabric Using Nanoindetation

Popis výsledku v původním jazyce

This paper is focused mainly on nanoindentation of carbon fibers. Fibers are in form of carbon fiber fabric that is used in larger research that is focused on reinforcing beams made of glued laminated timber. Knowledge of this material on macro and micro level will help to understand its behavior in this specific type of use. Nanoindentation is method used in this paper to obtain material characteristics on micro level such as hardness and modulus of elasticity. Samples of the carbon fiber fabric had to be prepared for this specific testing method by polishing samples of carbon fabric attached in epoxy resin. In particular, it was found that the indentation hardness of the fibers ranges around 3.65 GPa and modulus of elasticity ranges around 26 GPa.

Název v anglickém jazyce

Evaluation of Micromechanical Properties of Carbon Fiber Fabric Using Nanoindetation

Popis výsledku anglicky

This paper is focused mainly on nanoindentation of carbon fibers. Fibers are in form of carbon fiber fabric that is used in larger research that is focused on reinforcing beams made of glued laminated timber. Knowledge of this material on macro and micro level will help to understand its behavior in this specific type of use. Nanoindentation is method used in this paper to obtain material characteristics on micro level such as hardness and modulus of elasticity. Samples of the carbon fiber fabric had to be prepared for this specific testing method by polishing samples of carbon fabric attached in epoxy resin. In particular, it was found that the indentation hardness of the fibers ranges around 3.65 GPa and modulus of elasticity ranges around 26 GPa.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/LO1605" target="_blank" >LO1605: Univerzitní centrum energeticky efektivních budov – Fáze udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NMM 2017 - Nano & Macro Mechanics 2017

ISBN

978-80-01-06346-0

ISSN

—

e-ISSN

2336-5382

Počet stran výsledku

5

Strana od-do

66-70

Název nakladatele

Czech Technical University in Prague

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

21. 9. 2017

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000433365100012