STRENGTH SCALING FROM C-S-H GLOBULES TO CEMENT PASTE USING MULTISCALE HIERARCHICAL MODELING

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F18%3A00324318" target="_blank" >RIV/68407700:21110/18:00324318 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

STRENGTH SCALING FROM C-S-H GLOBULES TO CEMENT PASTE USING MULTISCALE HIERARCHICAL MODELING

Popis výsledku v původním jazyce

Strength scaling from C-S-H globules to cement paste using hierarchical modelling offers important insight into mechanics of stress transfer and strength. Recent results from molecular simulation, microbending tests, micromechanics and macroscale data allowed us to build a more consistent hierarchical model while having consistent strength properties at each level. The level of C-S-H can identify tensile strength of C-S-H globule as high as 2500 MPa, validating experimental results on submicrometer scale. Internal defects of mm size control substantially macroscopic strength properties in the pastes; this is demonstrated on a mature cement paste with w/c=0.35. Origin of internal defects lies likely in entrapped air and chemical shrinkage and they seem to be present in the majority of experimental samples. That is the main reason why unreinforced cementitious composites seldom exceed tensile strength of ~15 MPa.

Název v anglickém jazyce

STRENGTH SCALING FROM C-S-H GLOBULES TO CEMENT PASTE USING MULTISCALE HIERARCHICAL MODELING

Popis výsledku anglicky

Strength scaling from C-S-H globules to cement paste using hierarchical modelling offers important insight into mechanics of stress transfer and strength. Recent results from molecular simulation, microbending tests, micromechanics and macroscale data allowed us to build a more consistent hierarchical model while having consistent strength properties at each level. The level of C-S-H can identify tensile strength of C-S-H globule as high as 2500 MPa, validating experimental results on submicrometer scale. Internal defects of mm size control substantially macroscopic strength properties in the pastes; this is demonstrated on a mature cement paste with w/c=0.35. Origin of internal defects lies likely in entrapped air and chemical shrinkage and they seem to be present in the majority of experimental samples. That is the main reason why unreinforced cementitious composites seldom exceed tensile strength of ~15 MPa.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Workshop on Concrete Modelling and Materials Behaviour in honor of Professor Klaas van Breugel

ISBN

978-2-35158-214-5

ISSN

—

e-ISSN

—

Počet stran výsledku

11

Strana od-do

48-58

Název nakladatele

Rilem Publications s.a.r.l.

Místo vydání

Bagneux

Místo konání akce

Delft

Datum konání akce

26. 8. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—