SMALL SCALE FRACTURE PROPERTIES OF CEMENT PASTE AND ALKALI-ACTIVATED FLY ASH

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F18%3A00325913" target="_blank" >RIV/68407700:21110/18:00325913 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

SMALL SCALE FRACTURE PROPERTIES OF CEMENT PASTE AND ALKALI-ACTIVATED FLY ASH

Popis výsledku v původním jazyce

The paper shows novel methodology and quantitative results of small scale elastic and fracture properties of cement paste and alkali-activated fly ash constituents at the level of micrometers. Local Young’s moduli, tensile strengths and fracture energies are derived from nanoindentation and micro-beam bending on microscale specimens prepared with focused ion beam milling. It is shown that the main cement hydration products (inner and outer products) that are rich of C-S-H gel reach tensile strength of 260-700 MPa. N-A-S-H gel in alkaliactivated fly ash is characterized with the mean strength of 340 MPa. The values are several orders of magnitude higher compared to their macroscopic counterparts. Supremum fracture energies were found in the range 4-20 J/m2 on individual microstructural components.

Název v anglickém jazyce

SMALL SCALE FRACTURE PROPERTIES OF CEMENT PASTE AND ALKALI-ACTIVATED FLY ASH

Popis výsledku anglicky

The paper shows novel methodology and quantitative results of small scale elastic and fracture properties of cement paste and alkali-activated fly ash constituents at the level of micrometers. Local Young’s moduli, tensile strengths and fracture energies are derived from nanoindentation and micro-beam bending on microscale specimens prepared with focused ion beam milling. It is shown that the main cement hydration products (inner and outer products) that are rich of C-S-H gel reach tensile strength of 260-700 MPa. N-A-S-H gel in alkaliactivated fly ash is characterized with the mean strength of 340 MPa. The values are several orders of magnitude higher compared to their macroscopic counterparts. Supremum fracture energies were found in the range 4-20 J/m2 on individual microstructural components.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA17-05360S" target="_blank" >GA17-05360S: Lomové vlastnosti amorfních a krystalických materiálů stanovené pomocí nanoindentace a fokusovaného iontového svazku v malém měřítku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

SynerCrete'18

ISBN

978-2-35158-202-2

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

779-784

Název nakladatele

Rilem Publications s.a.r.l.

Místo vydání

Bagneux

Místo konání akce

Funchal

Datum konání akce

24. 10. 2018

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—