Rheological properties of alkali-activated brick powder based pastes: Effect of alkali activator and silicate modulus

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F18%3A00328182" target="_blank" >RIV/68407700:21110/18:00328182 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26110/18:PU128245

Výsledek na webu

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.276.185" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.276.185</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.276.185" target="_blank" >10.4028/www.scientific.net/SSP.276.185</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Rheological properties of alkali-activated brick powder based pastes: Effect of alkali activator and silicate modulus

Popis výsledku v původním jazyce

The rheological behaviour of alkali-activated materials prepared by activation of a brick powder by alkaline solution (alkali + water glass) is described. The influence of the composition of activation solution (NaOH vs. KOH, varied silicate modulus) on the flow properties (yield stress, consistency coefficient, fluidity index) and the evolution of the elastic modulus (G ') and the viscous modulus (G ' ') over time were studied. The rheological characterization was completed by frequency sweep tests with the aim of investigating the material behaviour more in detail. The results show that the pastes are thixotropic suspensions with very low yield stress. The potassium activator decreases the yield stress and viscosity of the pastes and retards the polymerization kinetic. The brick pastes become more rigid and more viscous with increasing silicate modulus. This also leads to an acceleration of gel formation in brick pastes.

Název v anglickém jazyce

Rheological properties of alkali-activated brick powder based pastes: Effect of alkali activator and silicate modulus

Popis výsledku anglicky

The rheological behaviour of alkali-activated materials prepared by activation of a brick powder by alkaline solution (alkali + water glass) is described. The influence of the composition of activation solution (NaOH vs. KOH, varied silicate modulus) on the flow properties (yield stress, consistency coefficient, fluidity index) and the evolution of the elastic modulus (G ') and the viscous modulus (G ' ') over time were studied. The rheological characterization was completed by frequency sweep tests with the aim of investigating the material behaviour more in detail. The results show that the pastes are thixotropic suspensions with very low yield stress. The potassium activator decreases the yield stress and viscosity of the pastes and retards the polymerization kinetic. The brick pastes become more rigid and more viscous with increasing silicate modulus. This also leads to an acceleration of gel formation in brick pastes.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Solid State Phenomena

ISBN

9783035713480

ISSN

1662-9779

e-ISSN

—

Počet stran výsledku

7

Strana od-do

185-191

Název nakladatele

TRANS TECH PUBLICATIONS LTD

Místo vydání

Zurich

Místo konání akce

Brno

Datum konání akce

7. 12. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—