The influence of fibre orientation on the mechanical properties of cement composites
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F19%3A00334143" target="_blank" >RIV/68407700:21110/19:00334143 - isvavai.cz</a>
Výsledek na webu
<a href="https://bookshelf.vitalsource.com/books/9780429761171" target="_blank" >https://bookshelf.vitalsource.com/books/9780429761171</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1201/9780429426506-259" target="_blank" >10.1201/9780429426506-259</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The influence of fibre orientation on the mechanical properties of cement composites
Popis výsledku v původním jazyce
This paper is focused on fibre orientation in cementitious composites. The purpose of this research was to verify the influence of the casting direction of the cement composite fibre-reinforced mixture into the formwork on the final fibre orientation and on the mechanical properties of the hardened concrete. The influence of two perpendicular casting direction (to make horizontally and vertically formed samples) on fibre reinforced cementitious composites and mechanical parameters was experimentally confirmed. Tensile strength and specific fracture energy of samples with different casting direction were compared by three-point bending test. Test results and evaluation of measurement data were performed by means of the specific fracture energy values. The reference mixture was made of the same composition without steel fibres to compare results.
Název v anglickém jazyce
The influence of fibre orientation on the mechanical properties of cement composites
Popis výsledku anglicky
This paper is focused on fibre orientation in cementitious composites. The purpose of this research was to verify the influence of the casting direction of the cement composite fibre-reinforced mixture into the formwork on the final fibre orientation and on the mechanical properties of the hardened concrete. The influence of two perpendicular casting direction (to make horizontally and vertically formed samples) on fibre reinforced cementitious composites and mechanical parameters was experimentally confirmed. Tensile strength and specific fracture energy of samples with different casting direction were compared by three-point bending test. Test results and evaluation of measurement data were performed by means of the specific fracture energy values. The reference mixture was made of the same composition without steel fibres to compare results.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Advances in Engineering Materials, Structures and Systems: Innovations, Mechanics and Applications
ISBN
978-0-429-42650-6
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
1501-1505
Název nakladatele
Taylor & Francis Group
Místo vydání
Londýn
Místo konání akce
Cape Town
Datum konání akce
2. 9. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000504648100259