Influence of Compression Pressure on Thermal Expansion, Bulk Density, and Porosity of Electroporcelain after Firing

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F20%3A00342927" target="_blank" >RIV/68407700:21110/20:00342927 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1063/5.0025878" target="_blank" >https://doi.org/10.1063/5.0025878</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1063/5.0025878" target="_blank" >10.1063/5.0025878</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Compression Pressure on Thermal Expansion, Bulk Density, and Porosity of Electroporcelain after Firing

Popis výsledku v původním jazyce

The influence of the compression pressure on the thermal expansion, bulk density, and porosity of electroporcelain type C 130 made under the pressures of 70 MPa, 90 MPa, and 110 MPa is studied after firing up to 1400 °C by a step of 100 °C. The mass loss and shrinkage of samples decreases with the compression pressure. The bulk density of the studied samples differs to a very little extent. At the firing temperature of 1400 °C, the lowest porosity is obtained for the sample pressed under the highest compression pressure. At 1300 °C, which is the common temperature for electroporcelain production, the lowest porosity is for the sample pressed at 90 MPa.

Název v anglickém jazyce

Influence of Compression Pressure on Thermal Expansion, Bulk Density, and Porosity of Electroporcelain after Firing

Popis výsledku anglicky

The influence of the compression pressure on the thermal expansion, bulk density, and porosity of electroporcelain type C 130 made under the pressures of 70 MPa, 90 MPa, and 110 MPa is studied after firing up to 1400 °C by a step of 100 °C. The mass loss and shrinkage of samples decreases with the compression pressure. The bulk density of the studied samples differs to a very little extent. At the firing temperature of 1400 °C, the lowest porosity is obtained for the sample pressed under the highest compression pressure. At 1300 °C, which is the common temperature for electroporcelain production, the lowest porosity is for the sample pressed at 90 MPa.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

AIP Conference Proceedings 2275

ISBN

978-0-7354-4005-0

ISSN

—

e-ISSN

1551-7616

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

AIP Publishing, APL, the American Institute of Physics

Místo vydání

Melville, NY

Místo konání akce

Eger

Datum konání akce

2. 9. 2020

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—