Microscopic analysis of composite boards made from rapeseed straw particles
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F21%3A00343905" target="_blank" >RIV/68407700:21110/21:00343905 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.1063/5.0047799" target="_blank" >https://doi.org/10.1063/5.0047799</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1063/5.0047799" target="_blank" >10.1063/5.0047799</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microscopic analysis of composite boards made from rapeseed straw particles
Popis výsledku v původním jazyce
The purpose of the research was to evaluate the possibilities of using an environmental-friendly adhesive for the preparation of composite boards from rapeseed straw. Rapeseed straw surface was untreated, hydrothermally treated and treated with an alkaline solution. Bone adhesive mixed with sodium lignosulfonate in a 6:1 ratio was used as the adhesive mixture. Based on microscopic analysis of failure modes in the adhesive joints of the produced boards, it was verified that the bone adhesive modified via the addition of sodium lignosulfonate can be successfully used for the production of composite boards from rapeseed straw. The most suitable surface treatment of rapeseed straw for the chosen type of adhesive mixture is soaking rapeseed straw in 2% sodium hydroxide solution.
Název v anglickém jazyce
Microscopic analysis of composite boards made from rapeseed straw particles
Popis výsledku anglicky
The purpose of the research was to evaluate the possibilities of using an environmental-friendly adhesive for the preparation of composite boards from rapeseed straw. Rapeseed straw surface was untreated, hydrothermally treated and treated with an alkaline solution. Bone adhesive mixed with sodium lignosulfonate in a 6:1 ratio was used as the adhesive mixture. Based on microscopic analysis of failure modes in the adhesive joints of the produced boards, it was verified that the bone adhesive modified via the addition of sodium lignosulfonate can be successfully used for the production of composite boards from rapeseed straw. The most suitable surface treatment of rapeseed straw for the chosen type of adhesive mixture is soaking rapeseed straw in 2% sodium hydroxide solution.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)
Návaznosti výsledku
Projekt
<a href="/cs/project/GA20-12166S" target="_blank" >GA20-12166S: Charakterizace kompozitních materiálů na bázi povrchově modifikované řepkové slámy a ekologicky šetrných lepidel</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
AIP Conference Proceedings 2343
ISBN
9780735440883
ISSN
0094-243X
e-ISSN
—
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
American Institute of Physics
Místo vydání
Melville, New York
Místo konání akce
Heraklion
Datum konání akce
29. 4. 2020
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—