Thermal Expansion of Illitic Clay and CaCO3 Mixtures During Thermal Treatment up to 1200 °C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F23%3A00373865" target="_blank" >RIV/68407700:21110/23:00373865 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1063/5.0146750" target="_blank" >https://doi.org/10.1063/5.0146750</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1063/5.0146750" target="_blank" >10.1063/5.0146750</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Thermal Expansion of Illitic Clay and CaCO3 Mixtures During Thermal Treatment up to 1200 °C

Popis výsledku v původním jazyce

The paper deals with thermodilatometric analysis of illitic clay – calcium carbonate mixtures. The samples are made by dry pressing from a mixture of illitic clay and CaCO3 with 6% addition of polyvinyl alcohol in the form of 3% solution. Polyvinyl alcohol-free samples are also produced. Samples with different CaCO3 contents, namely 17.6%, 21.6%, and 25.6%, are used for the measurements. Thermodilatometry measurements is performed using a horizontal push-rod corundum dilatometer in the temperature range from 30 °C to 1200 °C with a linear heating rate of 5 °C/min. The influence of polyvinyl alcohol and the amount of CaCO3 on the relative thermal expansion of the samples is investigated. The most satisfactory result of relative thermal expansion is found in the case of samples with polyvinyl alcohol and with CaCO3 content of 21.6 %, where the relative expansion recorded at 1200 °C is 1%.

Název v anglickém jazyce

Thermal Expansion of Illitic Clay and CaCO3 Mixtures During Thermal Treatment up to 1200 °C

Popis výsledku anglicky

The paper deals with thermodilatometric analysis of illitic clay – calcium carbonate mixtures. The samples are made by dry pressing from a mixture of illitic clay and CaCO3 with 6% addition of polyvinyl alcohol in the form of 3% solution. Polyvinyl alcohol-free samples are also produced. Samples with different CaCO3 contents, namely 17.6%, 21.6%, and 25.6%, are used for the measurements. Thermodilatometry measurements is performed using a horizontal push-rod corundum dilatometer in the temperature range from 30 °C to 1200 °C with a linear heating rate of 5 °C/min. The influence of polyvinyl alcohol and the amount of CaCO3 on the relative thermal expansion of the samples is investigated. The most satisfactory result of relative thermal expansion is found in the case of samples with polyvinyl alcohol and with CaCO3 content of 21.6 %, where the relative expansion recorded at 1200 °C is 1%.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

<a href="/cs/project/GA20-01536S" target="_blank" >GA20-01536S: Řízená modifikace mineralogického složení keramického střepu za účelem zlepšení jeho užitných vlastností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Central European Symposium on Thermophysics 2022 (CEST 2022)

ISBN

—

ISSN

1551-7616

e-ISSN

1551-7616

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

AIP Conference Proceedings

Místo vydání

New York

Místo konání akce

Olomouc

Datum konání akce

31. 8. 2022

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—