Effect of Fineness and Addition Levels of Low-Grade Czech Clay on the Microstructure and Compressive Strength of Calcined Clay-Limestone Cement

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F25%3A00384023" target="_blank" >RIV/68407700:21110/25:00384023 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1007/978-3-031-83889-7_17" target="_blank" >https://doi.org/10.1007/978-3-031-83889-7_17</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/978-3-031-83889-7_17" target="_blank" >10.1007/978-3-031-83889-7_17</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of Fineness and Addition Levels of Low-Grade Czech Clay on the Microstructure and Compressive Strength of Calcined Clay-Limestone Cement

Popis výsledku v původním jazyce

This study explores the feasibility of utilizing local Czech clay from the Kadaň area, with a yield of ~35% kaolin from the clay matrix, to produce limestone calcined clay cement (LC3). The raw clay was first ground using a laboratory-scale disk mill to achieve different fineness and then calcined at 800 °C. Pozzolanic activity of calcined clay was assessed using an accelerated R3 pozzolanic test. The effect of the fineness of raw clay on the microstructure development and the compressive strength of LC3 with 20, 35, and 50% cement replacement was studied at 28 days of hydration.

Název v anglickém jazyce

Effect of Fineness and Addition Levels of Low-Grade Czech Clay on the Microstructure and Compressive Strength of Calcined Clay-Limestone Cement

Popis výsledku anglicky

This study explores the feasibility of utilizing local Czech clay from the Kadaň area, with a yield of ~35% kaolin from the clay matrix, to produce limestone calcined clay cement (LC3). The raw clay was first ground using a laboratory-scale disk mill to achieve different fineness and then calcined at 800 °C. Pozzolanic activity of calcined clay was assessed using an accelerated R3 pozzolanic test. The effect of the fineness of raw clay on the microstructure development and the compressive strength of LC3 with 20, 35, and 50% cement replacement was studied at 28 days of hydration.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

<a href="/cs/project/GA20-14506S" target="_blank" >GA20-14506S: Metody pro zastavení hydratace cementu, vápna a sádry</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Calcined Clays for Sustainable Concrete: Proceedings of the International Conference on Calcined Clays for Sustainable Concrete 2022

ISBN

978-94-024-1207-9

ISSN

2211-0852

e-ISSN

2211-0852

Počet stran výsledku

9

Strana od-do

161-169

Název nakladatele

Springer Nature Switzerland AG

Místo vydání

Basel

Místo konání akce

Lausanne

Datum konání akce

5. 7. 2022

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—