Improvement of Wear Resistence of the PM Cr-V Ledeburitic Steel by Duplex Coating

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F02%3A02080749" target="_blank" >RIV/68407700:21220/02:02080749 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Improvement of Wear Resistence of the PM Cr-V Ledeburitic Steel by Duplex Coating
Popis výsledku v původním jazyce
The P/M made VANADIS 6 ledeburitic steel was heat treated, plasma nitrided and duplex coated at various combinations of processing parameters. The most important surface characteristics like microstructure, hardness profiles, nitrogen concentration depthprofiles, phase constitution and wear resistance have been investigated.
Název v anglickém jazyce
Improvement of Wear Resistence of the PM Cr-V Ledeburitic Steel by Duplex Coating
Popis výsledku anglicky
The P/M made VANADIS 6 ledeburitic steel was heat treated, plasma nitrided and duplex coated at various combinations of processing parameters. The most important surface characteristics like microstructure, hardness profiles, nitrogen concentration depthprofiles, phase constitution and wear resistance have been investigated.

Projekt
<a href="/cs/project/GA106%2F01%2F0180" target="_blank" >GA106/01/0180: Mechanismus a kinetika sycení multifázové Fe - C - Cr - V oceli dusíkem</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2002
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Popis výsledku