Fracture Behaviour of the Bazal Fibre Reinforced Composites with Polysiloxane-Derived Matrix
Popis výsledku v původním jazyce
Selected mechanical properties of unidirectional composites with polysiloxane-derived matrix and continuous basalt fibres reinforcement are presented. A secial attention is devoted to the impact of long term explosition in hot air to the composite failure under flexural load. The investigated composites worsened their properties after treatment in air at elevated temperature (650-750°C). The originally non-catastrophic flexural failure changed to a brittle fracture, which was accompanied with a flexuralstrength decrease.
Název v anglickém jazyce
Fracture Behaviour of the Bazal Fibre Reinforced Composites with Polysiloxane-Derived Matrix
Popis výsledku anglicky
Selected mechanical properties of unidirectional composites with polysiloxane-derived matrix and continuous basalt fibres reinforcement are presented. A secial attention is devoted to the impact of long term explosition in hot air to the composite failure under flexural load. The investigated composites worsened their properties after treatment in air at elevated temperature (650-750°C). The originally non-catastrophic flexural failure changed to a brittle fracture, which was accompanied with a flexuralstrength decrease.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—

Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)