Phase composition and morphology development in WE-type alloys modified by high Zn content

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F09%3A00148440" target="_blank" >RIV/68407700:21220/09:00148440 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Phase composition and morphology development in WE-type alloys modified by high Zn content

Popis výsledku v původním jazyce

Quasicrystalline icosahedral equilibrium phase was found in Mg-Y-Nd (WE43) alloys with the addition of 12 wt.% and 25 wt.% Zn constituting grain boundary eutectic phases. In response to the isochronal annealing morphologically similar precipitates of thephases with the same structure as those developing during heat treatment of binary Mg-8wt.%Zn alloy at temperatures higher than 150°C were observed, namely ?1' (b-centered monoclinic crystal structure a=2.596 nm, b=1.428 nm, c=0.524 nm, ?=102.5°) and ?2' (hexagonal MgZn2). Development of the resistivity and microhardness during isochronal annealing corresponds to the phase transformations and morphology changes of the phases observed. Dislocations with the c Burgers vector component generated due to the presence of icosahedral phase are responsible for the improved formability as compared to the WE43 alloy.

Název v anglickém jazyce

Phase composition and morphology development in WE-type alloys modified by high Zn content

Popis výsledku anglicky

Quasicrystalline icosahedral equilibrium phase was found in Mg-Y-Nd (WE43) alloys with the addition of 12 wt.% and 25 wt.% Zn constituting grain boundary eutectic phases. In response to the isochronal annealing morphologically similar precipitates of thephases with the same structure as those developing during heat treatment of binary Mg-8wt.%Zn alloy at temperatures higher than 150°C were observed, namely ?1' (b-centered monoclinic crystal structure a=2.596 nm, b=1.428 nm, c=0.524 nm, ?=102.5°) and ?2' (hexagonal MgZn2). Development of the resistivity and microhardness during isochronal annealing corresponds to the phase transformations and morphology changes of the phases observed. Dislocations with the c Burgers vector component generated due to the presence of icosahedral phase are responsible for the improved formability as compared to the WE43 alloy.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F0252" target="_blank" >GA106/06/0252: Vliv minoritních prvků na plasticitu slitin Mg se vzácnými zeminami</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Materials Research

ISSN

1862-5282

e-ISSN

—

Svazek periodika

100

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

000264870600005

EID výsledku v databázi Scopus

—