High temperature oxidation protective chromium-based coatings prepared by IBAD and PACVD methods
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F09%3A00155113" target="_blank" >RIV/68407700:21220/09:00155113 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
High temperature oxidation protective chromium-based coatings prepared by IBAD and PACVD methods
Popis výsledku v původním jazyce
Chromium nitride films were prepared by high energy (90 keV) IBAD method and chromium oxide films were prepared by PACVD method on AISI 316 stainless steel. The chemical composition was evaluated by electron beam microanalysis. The mechanical propertiesof coatings were tested by Vickers indenter, scratch tester and calotest. The films were hard and exhibited a satisfactory adhesion to the steel substrate. The corrosion resistance of the coatings was tested at 700-1000 °C in oxidizing atmosphere (air).The corrosion kinetics was evaluated by the gravimetric method. The total corrosion exposure was up to 1000 h. The films decreased high temperature oxidation of stainless steel substrates.
Název v anglickém jazyce
High temperature oxidation protective chromium-based coatings prepared by IBAD and PACVD methods
Popis výsledku anglicky
Chromium nitride films were prepared by high energy (90 keV) IBAD method and chromium oxide films were prepared by PACVD method on AISI 316 stainless steel. The chemical composition was evaluated by electron beam microanalysis. The mechanical propertiesof coatings were tested by Vickers indenter, scratch tester and calotest. The films were hard and exhibited a satisfactory adhesion to the steel substrate. The corrosion resistance of the coatings was tested at 700-1000 °C in oxidizing atmosphere (air).The corrosion kinetics was evaluated by the gravimetric method. The total corrosion exposure was up to 1000 h. The films decreased high temperature oxidation of stainless steel substrates.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Surface and Coatings Technology
ISSN
0257-8972
e-ISSN
—
Svazek periodika
203
Číslo periodika v rámci svazku
17-18
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
—
Kód UT WoS článku
000266682000051
EID výsledku v databázi Scopus
—