Flexural strength and modulus of nanofilled and low-shrinkage dental restorative composites: Three-point bending test.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F09%3A00158402" target="_blank" >RIV/68407700:21220/09:00158402 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Flexural strength and modulus of nanofilled and low-shrinkage dental restorative composites: Three-point bending test.

Popis výsledku v původním jazyce

Most common failure of dental composite filler was caused by restoration fracture and secondary caries. The reasons of failure under occlusal load were attributed to the high stress at the toothrestoration interface. The cavity shape could influence themagnitude of the interfacial stress. Using finite element program cavity design could be solved through the cavity shape optimization analysis that required exact material properties. In this study, flexural strength and flexural modulus of two composites (FiltekTM Silorane and FiltekTM Superme XT) were determined by three-point bending test.

Název v anglickém jazyce

Flexural strength and modulus of nanofilled and low-shrinkage dental restorative composites: Three-point bending test.

Popis výsledku anglicky

Most common failure of dental composite filler was caused by restoration fracture and secondary caries. The reasons of failure under occlusal load were attributed to the high stress at the toothrestoration interface. The cavity shape could influence themagnitude of the interfacial stress. Using finite element program cavity design could be solved through the cavity shape optimization analysis that required exact material properties. In this study, flexural strength and flexural modulus of two composites (FiltekTM Silorane and FiltekTM Superme XT) were determined by three-point bending test.

Druh

D - Stať ve sborníku

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

10th Workshop on Applied Mechanics Proceeding

ISBN

978-80-01-04332-5

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

—

Název nakladatele

Department of Mechanics, Biomechanics and Mechatronics; Faculty of Mechanical Engineering; CTU in Prague

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

11. 2. 2009

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—