Nanoindentation of dental composites
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F10%3A00170801" target="_blank" >RIV/68407700:21220/10:00170801 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Nanoindentation of dental composites
Popis výsledku v původním jazyce
The intent of this study was to evaluate elastic modulus of different dental filling composites. Nanoindentation was focused on mechanical properties of upper irradiated layers of the specimens and on deeper layers where the intensity of polymerization radiation decreased. In order to observe effect of time on indentation modulus different time intervals between nanoindentations were determined after specimen manufacturing. Static and dynamic analyses were performed using a Hysitron's TriboLab?. Each tested material presented significant increase in modulus after 1 week and moderate decrease in the following days. Lower intensity of radiation due to light absorption caused moderate decrease of elastic modulus. The viscoelastic properties of compositesare weak.
Název v anglickém jazyce
Nanoindentation of dental composites
Popis výsledku anglicky
The intent of this study was to evaluate elastic modulus of different dental filling composites. Nanoindentation was focused on mechanical properties of upper irradiated layers of the specimens and on deeper layers where the intensity of polymerization radiation decreased. In order to observe effect of time on indentation modulus different time intervals between nanoindentations were determined after specimen manufacturing. Static and dynamic analyses were performed using a Hysitron's TriboLab?. Each tested material presented significant increase in modulus after 1 week and moderate decrease in the following days. Lower intensity of radiation due to light absorption caused moderate decrease of elastic modulus. The viscoelastic properties of compositesare weak.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Human Biomechanics 2010
ISBN
978-80-7372-648-5
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
—
Název nakladatele
Technical University of Liberec
Místo vydání
Liberec
Místo konání akce
Sychrov
Datum konání akce
4. 10. 2010
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—