Heat Treatment of Cr-V Ledeburitic Steel Substrate for Plasma Nitriding

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F10%3A00172341" target="_blank" >RIV/68407700:21220/10:00172341 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Heat Treatment of Cr-V Ledeburitic Steel Substrate for Plasma Nitriding
Popis výsledku v původním jazyce
The Vanadis 6 PM ledeburitic steel was chosen as a substrate for further plasma nitriding. The material was austenitised, quenched and double tempered to 57-58 HRC. Some specimens were also sub-zero treated in order to improve the transformation of the austenite to martensite. The microstructure of heat processed steel was examined by optical microscopy and scanning electron microscopy. The resistance against nucleation of fracture was assessed by the three point bending strength test and the fracture surfaces were subjected to fractographical analysis.
Název v anglickém jazyce
Heat Treatment of Cr-V Ledeburitic Steel Substrate for Plasma Nitriding
Popis výsledku anglicky
The Vanadis 6 PM ledeburitic steel was chosen as a substrate for further plasma nitriding. The material was austenitised, quenched and double tempered to 57-58 HRC. Some specimens were also sub-zero treated in order to improve the transformation of the austenite to martensite. The microstructure of heat processed steel was examined by optical microscopy and scanning electron microscopy. The resistance against nucleation of fracture was assessed by the three point bending strength test and the fracture surfaces were subjected to fractographical analysis.

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
SEMDOK 2010 - 15th Internationl of PhD. students' seminare
ISBN
978-80-554-0157-7
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
žilinská universita, Strojnícka fakulta
Místo vydání
žilina
Místo konání akce
Těrchová
Datum konání akce
27. 1. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—

Podobné výsledky(10)