Influence of Thermal and Thermo-mechanical Processing on the Creep Resistance of Mg-10Gd-3Y-0,4Zr Alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F11%3A00177768" target="_blank" >RIV/68407700:21220/11:00177768 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Thermal and Thermo-mechanical Processing on the Creep Resistance of Mg-10Gd-3Y-0,4Zr Alloy

Popis výsledku v původním jazyce

Alloy Mg-10Gd-3Y-0,4Zr in as-cast, as-extruded, cast-T6 (peak aged) and extruded-T5 (peak aged) state was tensile creep tested at 200, 250 and 300°C and stress 50, 80 and 120 MPa. Comparison of minimal creep rate shows that alloy Mg-10Gd-3Y-0,4Zr in cast-T6 conditions is characterized by an excellent creep resistance, which is higher than that of commercially available Mg-alloys. Creep resistance of as-cast, as-extruded and extruded-T5 alloy Mg-10Gd-3Y-0,4Zr is lower. Cavity nucleation is heavily affected by the amount of secondary phases on the grain boundaries and also by the initial grain size of the microstructure. After extrusion and in the extruded-T5 conditions creep cavitation was not observed, whereas in the as-cast and cast-T6 conditions creep cavitation occurred on the high fraction of grain boundaries.

Název v anglickém jazyce

Influence of Thermal and Thermo-mechanical Processing on the Creep Resistance of Mg-10Gd-3Y-0,4Zr Alloy

Popis výsledku anglicky

Alloy Mg-10Gd-3Y-0,4Zr in as-cast, as-extruded, cast-T6 (peak aged) and extruded-T5 (peak aged) state was tensile creep tested at 200, 250 and 300°C and stress 50, 80 and 120 MPa. Comparison of minimal creep rate shows that alloy Mg-10Gd-3Y-0,4Zr in cast-T6 conditions is characterized by an excellent creep resistance, which is higher than that of commercially available Mg-alloys. Creep resistance of as-cast, as-extruded and extruded-T5 alloy Mg-10Gd-3Y-0,4Zr is lower. Cavity nucleation is heavily affected by the amount of secondary phases on the grain boundaries and also by the initial grain size of the microstructure. After extrusion and in the extruded-T5 conditions creep cavitation was not observed, whereas in the as-cast and cast-T6 conditions creep cavitation occurred on the high fraction of grain boundaries.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science Forum

ISSN

0255-5476

e-ISSN

—

Svazek periodika

???

Číslo periodika v rámci svazku

675

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

487-490

Kód UT WoS článku

000297036200115

EID výsledku v databázi Scopus

—