Hot Cracking T-joint Weldability Test of Precipitation Hardenable Al Alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F11%3A00186150" target="_blank" >RIV/68407700:21220/11:00186150 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21260/11:00186150

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hot Cracking T-joint Weldability Test of Precipitation Hardenable Al Alloys

Popis výsledku v původním jazyce

This article presents research of weldability of aluminium alloys. The research was done at Faculty of Mechanical Engineering, CTU in Prague. In the rolling stock production often used precipitation hardenable Al alloy AlMg1Si1Mn was subjected to the hotcracking weldability test to research its susceptibility to hot cracking during GMAW. Base material and 3 recommended filler wires are subjected to T-joint weld cracking test. As filler wires AlSi5, AlMg4.5MnZr and AlMg5Cr were selected and welding method is GMAW. T-joint weld cracking test is usable test standardized for evaluation of hot cracking, but as the result of this research it was found, that its sensitivity is very low and other weldability test has to be used to asses weldability properly.

Název v anglickém jazyce

Hot Cracking T-joint Weldability Test of Precipitation Hardenable Al Alloys

Popis výsledku anglicky

This article presents research of weldability of aluminium alloys. The research was done at Faculty of Mechanical Engineering, CTU in Prague. In the rolling stock production often used precipitation hardenable Al alloy AlMg1Si1Mn was subjected to the hotcracking weldability test to research its susceptibility to hot cracking during GMAW. Base material and 3 recommended filler wires are subjected to T-joint weld cracking test. As filler wires AlSi5, AlMg4.5MnZr and AlMg5Cr were selected and welding method is GMAW. T-joint weld cracking test is usable test standardized for evaluation of hot cracking, but as the result of this research it was found, that its sensitivity is very low and other weldability test has to be used to asses weldability properly.

Druh

D - Stať ve sborníku

CEP obor

JR - Ostatní strojírenství

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Annals of DAAAM for 2011 and Proceedings

ISBN

978-3-901509-83-4

ISSN

1726-9679

e-ISSN

—

Počet stran výsledku

12

Strana od-do

633-644

Název nakladatele

DAAAM International

Místo vydání

Vienna

Místo konání akce

Vídeň

Datum konání akce

23. 11. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—