Relationships between the fretting wear behavior and mechanical properties of thin carbon films

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F12%3A00181581" target="_blank" >RIV/68407700:21220/12:00181581 - isvavai.cz</a>

Výsledek na webu

<a href="http://80.www.sciencedirect.com.dialog.cvut.cz/science/article/pii/S0042207X11002491" target="_blank" >http://80.www.sciencedirect.com.dialog.cvut.cz/science/article/pii/S0042207X11002491</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.vacuum.2011.07.011" target="_blank" >10.1016/j.vacuum.2011.07.011</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Relationships between the fretting wear behavior and mechanical properties of thin carbon films

Popis výsledku v původním jazyce

Mechanical load can drastically affect the properties of orthopedic implants materials. Damage of these materials usually occurs in contact surfaces, caused by abrasion, adhesion, fretting, delamination, pitting and fatigue depending on friction, lubrication, contact area, surface finish and level of loads (stresses). The good performance of the hard carbon coatings is often discussed. Results from this study of fretting and the associated lubrication (bovine serum) show that ta-C coatings, despite their high hardness, have very low friction coefficients and low volume losses.

Název v anglickém jazyce

Relationships between the fretting wear behavior and mechanical properties of thin carbon films

Popis výsledku anglicky

Mechanical load can drastically affect the properties of orthopedic implants materials. Damage of these materials usually occurs in contact surfaces, caused by abrasion, adhesion, fretting, delamination, pitting and fatigue depending on friction, lubrication, contact area, surface finish and level of loads (stresses). The good performance of the hard carbon coatings is often discussed. Results from this study of fretting and the associated lubrication (bovine serum) show that ta-C coatings, despite their high hardness, have very low friction coefficients and low volume losses.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

VACUUM

ISSN

0042-207X

e-ISSN

—

Svazek periodika

2012

Číslo periodika v rámci svazku

86

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

675-680

Kód UT WoS článku

000301018400022

EID výsledku v databázi Scopus

—