Synthesis of Zinc Polytetrafluorethylene Composite Coatings Based on Electroplating
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F12%3A00202920" target="_blank" >RIV/68407700:21220/12:00202920 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00010669:_____/12:#0001283
Výsledek na webu
<a href="http://pig.sagepub.com/content/early/2012/02/29/0954410012437506" target="_blank" >http://pig.sagepub.com/content/early/2012/02/29/0954410012437506</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1177/0954410012437506" target="_blank" >10.1177/0954410012437506</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Synthesis of Zinc Polytetrafluorethylene Composite Coatings Based on Electroplating
Popis výsledku v původním jazyce
This article covers the development of the synthesis of the zinc coatings with dispersed polytetrafluorethylene particles (zinc-polytetrafluorethylene composite coatings). The technology was based on zinc electrolytic plating in weakly acid bath. After optimising the parameters of the technology according to the results of coating analyses by infrared spectroscopy and tribological measurements, it was possible to prepare zinc coatings with homogenously incorporated polytetrafluorethylene. This ensured significantly lower friction coefficient of these coatings in comparison with pure zinc coating. The corrosion resistance and self-lubrication character of zinc-polytetrafluorethylene coatings is promising in potential replacement of existing multi-layered zinc coating systems.
Název v anglickém jazyce
Synthesis of Zinc Polytetrafluorethylene Composite Coatings Based on Electroplating
Popis výsledku anglicky
This article covers the development of the synthesis of the zinc coatings with dispersed polytetrafluorethylene particles (zinc-polytetrafluorethylene composite coatings). The technology was based on zinc electrolytic plating in weakly acid bath. After optimising the parameters of the technology according to the results of coating analyses by infrared spectroscopy and tribological measurements, it was possible to prepare zinc coatings with homogenously incorporated polytetrafluorethylene. This ensured significantly lower friction coefficient of these coatings in comparison with pure zinc coating. The corrosion resistance and self-lubrication character of zinc-polytetrafluorethylene coatings is promising in potential replacement of existing multi-layered zinc coating systems.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI1%2F047" target="_blank" >FR-TI1/047: *Vývoj komplexních, ekologicky přijatelných technologií kompozitních povrchových úprav na bázi zinku s nízkým koeficientem tření</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Proceedings of the Institution of Mechanical Engineers, Part G; Journal of Aerospace Engineering
ISSN
2041-3025
e-ISSN
—
Svazek periodika
2012
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
8
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—