Phase segregation during processing of semi-solid slurry by rheocasting method SEED

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F15%3A00233232" target="_blank" >RIV/68407700:21220/15:00233232 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
čeština
Název v původním jazyce
Phase segregation during processing of semi-solid slurry by rheocasting method SEED
Popis výsledku v původním jazyce
The paper describes specific phenomena of semi-solid casting process, especially rheo-casting method SEED, which uses mechanical swirling for reaching proper structure in semi-solid state. The eutectic segregation during processing of semi-solid slurry can cause specific casting defects. Heat treated alloy AlSi7Mg0.3 was applied for producing castings. For observing structure, metallographic observation by light and SEM microscopy was used as well as spectral analysis.
Název v anglickém jazyce
Phase segregation during processing of semi-solid slurry by rheocasting method SEED
Popis výsledku anglicky
The paper describes specific phenomena of semi-solid casting process, especially rheo-casting method SEED, which uses mechanical swirling for reaching proper structure in semi-solid state. The eutectic segregation during processing of semi-solid slurry can cause specific casting defects. Heat treated alloy AlSi7Mg0.3 was applied for producing castings. For observing structure, metallographic observation by light and SEM microscopy was used as well as spectral analysis.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)