Evolution of the nitrogen depth distribution in an implanted titanium alloy with a surface carbon nanolayer

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F17%3A00313813" target="_blank" >RIV/68407700:21220/17:00313813 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S0009261417303809" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0009261417303809</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.cplett.2017.04.066" target="_blank" >10.1016/j.cplett.2017.04.066</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Evolution of the nitrogen depth distribution in an implanted titanium alloy with a surface carbon nanolayer

Popis výsledku v původním jazyce

The impact of the thickness of the carbon nanolayer on the depth distribution of the implanted nitrogen was examined. Ti6Al4V samples with a carbon nanolayer (20 and 40 nm) were implanted with nitrogen with fluence of 1.2 . 10(17) cm(-2) and an accelerating voltage of 90 kV. GD-OES measurements showed an almost Gaussian-like nitrogen depth profile. The nitrogen peak moves deeper into the sample with increasing thickness of the nanolayer. The experimental depth profiles are in good agreement with the calculated results from the analytical model and from the SRIM2013 code.

Název v anglickém jazyce

Evolution of the nitrogen depth distribution in an implanted titanium alloy with a surface carbon nanolayer

Popis výsledku anglicky

The impact of the thickness of the carbon nanolayer on the depth distribution of the implanted nitrogen was examined. Ti6Al4V samples with a carbon nanolayer (20 and 40 nm) were implanted with nitrogen with fluence of 1.2 . 10(17) cm(-2) and an accelerating voltage of 90 kV. GD-OES measurements showed an almost Gaussian-like nitrogen depth profile. The nitrogen peak moves deeper into the sample with increasing thickness of the nanolayer. The experimental depth profiles are in good agreement with the calculated results from the analytical model and from the SRIM2013 code.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/GA16-22276S" target="_blank" >GA16-22276S: Dusíkem dopované titanové materiály: Studium teplotně závislé dopace v radiačně poškozené matrici</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemical Physics Letters

ISSN

0009-2614

e-ISSN

1873-4448

Svazek periodika

679

Číslo periodika v rámci svazku

July

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

6

Strana od-do

25-30

Kód UT WoS článku

000405403900005

EID výsledku v databázi Scopus

2-s2.0-85018266378