The Analysis of Causes of the Damage of a Turbine Blade Made of Ti-6Al-4V Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F17%3A00316179" target="_blank" >RIV/68407700:21220/17:00316179 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.270.189" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.270.189</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.270.189" target="_blank" >10.4028/www.scientific.net/SSP.270.189</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Analysis of Causes of the Damage of a Turbine Blade Made of Ti-6Al-4V Alloy
Popis výsledku v původním jazyce
The main causes of the damage of a compressor’s turbine blade are documented and described in the article. The turbine blade was made from titanium alloy grade 5 (VT6, Ti-6Al-4V). The analysed segments of the turbine blade were damaged by corrosion and erosion. The sample from the damaged blade was compared with an undamaged reference sample. The observed substantial distinctions between microstructure of the damaged and the reference sample were found using of light and scanning electron microscopy. The observed distinctions of the microstructure were caused by the differences in the heat treatment process.
Název v anglickém jazyce
The Analysis of Causes of the Damage of a Turbine Blade Made of Ti-6Al-4V Alloy
Popis výsledku anglicky
The main causes of the damage of a compressor’s turbine blade are documented and described in the article. The turbine blade was made from titanium alloy grade 5 (VT6, Ti-6Al-4V). The analysed segments of the turbine blade were damaged by corrosion and erosion. The sample from the damaged blade was compared with an undamaged reference sample. The observed substantial distinctions between microstructure of the damaged and the reference sample were found using of light and scanning electron microscopy. The observed distinctions of the microstructure were caused by the differences in the heat treatment process.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1207" target="_blank" >LO1207: Podpora udržitelnosti Inovačního centra diagnostiky a aplikace materiálů na ČVUT-FS v Praze</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Contribution of Metallography to Production Problem Solutions II
ISBN
978-3-0357-1241-4
ISSN
1662-9779
e-ISSN
—
Počet stran výsledku
5
Strana od-do
189-193
Název nakladatele
Trans Tech Publications
Místo vydání
Zurich
Místo konání akce
Mariánské Lázně
Datum konání akce
6. 6. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—