Crystallite size and microstrain evolution in low-temperature annealed titanium
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F20%3A00345073" target="_blank" >RIV/68407700:21220/20:00345073 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.37904/nanocon.2019.8706" target="_blank" >http://dx.doi.org/10.37904/nanocon.2019.8706</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.37904/nanocon.2019.8706" target="_blank" >10.37904/nanocon.2019.8706</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crystallite size and microstrain evolution in low-temperature annealed titanium
Popis výsledku v původním jazyce
An in situ investigation has been carried out by X-ray diffraction of the evolution of the crystallite size and the microstrain of low-temperature annealed commercially pure titanium grade 2 in the state after machining and polishing. Annealing was performed in vacuum at a temperature of 300, 400 and 500 °C, with various dwell times. The results presented here demonstrate that annealing temperatures lead to a significant reduction in microstrain and enhanced crystallite growth. The effect of the dwell time is more pronounced at temperatures above 400 °C. The dwell time at a temperature of 300 °C affects the crystallite growth but produces no microstrain relaxation. The presented results can be very useful for optimizing the working cycle and cooling during surface modification of titanium or exposed machines parts in order to improve the stability of the microstructure and extend the lifetime of components.
Název v anglickém jazyce
Crystallite size and microstrain evolution in low-temperature annealed titanium
Popis výsledku anglicky
An in situ investigation has been carried out by X-ray diffraction of the evolution of the crystallite size and the microstrain of low-temperature annealed commercially pure titanium grade 2 in the state after machining and polishing. Annealing was performed in vacuum at a temperature of 300, 400 and 500 °C, with various dwell times. The results presented here demonstrate that annealing temperatures lead to a significant reduction in microstrain and enhanced crystallite growth. The effect of the dwell time is more pronounced at temperatures above 400 °C. The dwell time at a temperature of 300 °C affects the crystallite growth but produces no microstrain relaxation. The presented results can be very useful for optimizing the working cycle and cooling during surface modification of titanium or exposed machines parts in order to improve the stability of the microstructure and extend the lifetime of components.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings 11th International Conference on Nanomaterials - Research & Application
ISBN
978-80-87294-95-6
ISSN
2694-930X
e-ISSN
—
Počet stran výsledku
5
Strana od-do
103-107
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
16. 10. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—