The Failure of Carbon Fiber Reinforced Composite Analyzed by Acoustic Emission

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F20%3A00349984" target="_blank" >RIV/68407700:21220/20:00349984 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.scientific.net/DDF.405.205#" target="_blank" >https://www.scientific.net/DDF.405.205#</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/DDF.405.205" target="_blank" >10.4028/www.scientific.net/DDF.405.205</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The Failure of Carbon Fiber Reinforced Composite Analyzed by Acoustic Emission

Popis výsledku v původním jazyce

This paper focus on evaluation of behavior, damage and failure processes occurring during the loading cycles in the carbon fiber reinforced composite by acoustic emission method. Since acoustic emission is physical phenomenon that detects the released energy in form of waves spreading through the material due to stimulation of material by external or internal stress, it is possible to evaluate complex damage and failure processes. For that purpose, the standard and open holes tensile testing specimens with different number of plies were manufactured. Selected acoustic emission parameters were correlated with data obtained from mechanical test. Linear localization method together with signal analysis using Fast Fourier transform algorithm were used as another tool for detection and evaluation of spreading damage processes inside the composite during the load. Basic damage types inside the composite material were identified by metallographic analysis using light microscopy. More complex damage processes were observed on the fracture surface using stereomicroscopy and scanning electron microscopy.

Název v anglickém jazyce

The Failure of Carbon Fiber Reinforced Composite Analyzed by Acoustic Emission

Popis výsledku anglicky

This paper focus on evaluation of behavior, damage and failure processes occurring during the loading cycles in the carbon fiber reinforced composite by acoustic emission method. Since acoustic emission is physical phenomenon that detects the released energy in form of waves spreading through the material due to stimulation of material by external or internal stress, it is possible to evaluate complex damage and failure processes. For that purpose, the standard and open holes tensile testing specimens with different number of plies were manufactured. Selected acoustic emission parameters were correlated with data obtained from mechanical test. Linear localization method together with signal analysis using Fast Fourier transform algorithm were used as another tool for detection and evaluation of spreading damage processes inside the composite during the load. Basic damage types inside the composite material were identified by metallographic analysis using light microscopy. More complex damage processes were observed on the fracture surface using stereomicroscopy and scanning electron microscopy.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Defect and Diffusion Forum Vol. 405

ISBN

978-3-0357-1612-2

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

205-211

Název nakladatele

Scientific.net

Místo vydání

Durnten-Zurich

Místo konání akce

Nový Smokovec

Datum konání akce

24. 4. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—