Effect of Annealing on the Surface Hardness of High-Fluence Nitrogen Ion-Implanted Titanium

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F23%3A00366934" target="_blank" >RIV/68407700:21220/23:00366934 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.3390/ma16103837" target="_blank" >https://doi.org/10.3390/ma16103837</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma16103837" target="_blank" >10.3390/ma16103837</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of Annealing on the Surface Hardness of High-Fluence Nitrogen Ion-Implanted Titanium

Popis výsledku v původním jazyce

Commercially pure titanium grade II was kinetically nitrided by implanting nitrogen ions with a fluence in the range of (1–9)x10^17 cm-2 and ion energy of 90 keV. Post- implantation annealing in the temperature stability range of TiN (up to 600°C) shows hardness degradation for titanium implanted with high fluences above 6x10^17 cm-2, leading to nitrogen oversaturation. Temperature-induced redistribution of interstitially located nitrogen in the oversaturated lattice has been found to be the predominant hardness degradation mechanism. The impact of the annealing temperature on a change in surface hardness related to the applied fluence of implanted nitrogen has been demonstrated.

Název v anglickém jazyce

Effect of Annealing on the Surface Hardness of High-Fluence Nitrogen Ion-Implanted Titanium

Popis výsledku anglicky

Commercially pure titanium grade II was kinetically nitrided by implanting nitrogen ions with a fluence in the range of (1–9)x10^17 cm-2 and ion energy of 90 keV. Post- implantation annealing in the temperature stability range of TiN (up to 600°C) shows hardness degradation for titanium implanted with high fluences above 6x10^17 cm-2, leading to nitrogen oversaturation. Temperature-induced redistribution of interstitially located nitrogen in the oversaturated lattice has been found to be the predominant hardness degradation mechanism. The impact of the annealing temperature on a change in surface hardness related to the applied fluence of implanted nitrogen has been demonstrated.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

1996-1944

Svazek periodika

16

Číslo periodika v rámci svazku

10

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

10

Strana od-do

1-10

Kód UT WoS článku

000996920300001

EID výsledku v databázi Scopus

2-s2.0-85160429013